摘要
The crystal structure of silicate oxyapatite Ca2Y8Si6O26 was indexed as hexagonal,space group P63/m,a=0.93515 nm,c=0.67872 nm,α=β=90°,γ=120°,V=0.5138692 nm3.Three strong peaks located at 32.079o,32.595o,and 50.104o with d=2.7903,2.74649,1.8194 was in accordance with,(112),and(213) planes.The optimum concentration of Tb3+ in Ca2Y8Si6O26 to yield highest photoluminescence intensity was 10 mol.% of Y3+.The corresponding excitation spectrum consisted of an intense broad band from 220 to 260 nm.The photoluminescence measurements showed that the green emission originated from 5D4-7F5 was predominant in the measured range with strong doublet lines at 543 and 549 nm.
The crystal structure of silicate oxyapatite Ca2Y8Si6O26 was indexed as hexagonal,space group P63/m,a=0.93515 nm,c=0.67872 nm,α=β=90°,γ=120°,V=0.5138692 nm3.Three strong peaks located at 32.079o,32.595o,and 50.104o with d=2.7903,2.74649,1.8194 was in accordance with,(112),and(213) planes.The optimum concentration of Tb3+ in Ca2Y8Si6O26 to yield highest photoluminescence intensity was 10 mol.% of Y3+.The corresponding excitation spectrum consisted of an intense broad band from 220 to 260 nm.The photoluminescence measurements showed that the green emission originated from 5D4-7F5 was predominant in the measured range with strong doublet lines at 543 and 549 nm.
基金
Project supported by the Natural Science Foundation of Jiangxi Province (2009GQC0042)
Foundation of Jiangxi Educational Committee (GJJ10153)
Foundation of Jiangxi University of Science and Technology (Jxxjzd10007)
Key Scientific and Technological Project of Henan Province (082102210049)