The feasibility to use electron beam welding to join the nominal compositionTi-48Al-2Cr-2Nb (at. percent) alloy was assessed. The microstructure characterization and crackingsusceptibility of the joints were evaluated by means of OM, SEM, XRD, and microhardness. It wasfound that the welded microstructure exhibited columnar and dendritic structures. Microstructuralconstituents in the fusion zone were a massive gamma structure and some amount of lamellar structureconsisting of alternating platelets of alpha_2 and gamma. The major contributing factor to thesusceptibility to solidification cracking was microsturctural change in this study for thesuppression of a phase decomposition leading to produce more retained alpha_2 brittle phase.Compared with transgranular cleavage fracture in the base metal, the weld metal exhibited mainlytranslamellar fracture.
The feasibility to use electron beam welding to join the nominal compositionTi-48Al-2Cr-2Nb (at. percent) alloy was assessed. The microstructure characterization and crackingsusceptibility of the joints were evaluated by means of OM, SEM, XRD, and microhardness. It wasfound that the welded microstructure exhibited columnar and dendritic structures. Microstructuralconstituents in the fusion zone were a massive gamma structure and some amount of lamellar structureconsisting of alternating platelets of alpha_2 and gamma. The major contributing factor to thesusceptibility to solidification cracking was microsturctural change in this study for thesuppression of a phase decomposition leading to produce more retained alpha_2 brittle phase.Compared with transgranular cleavage fracture in the base metal, the weld metal exhibited mainlytranslamellar fracture.
基金
ThisprojectisfinanciallysupportedbytheNationalHigh-TechResearchandDevelopmentProgramofChina(863Program,No.2002AA724040).