摘要
For the purpose of decreasing the applied limitation resulting from the anisotropic mechanical property of Al-Li alloy 2195, this study employed a complex heat treatment process, involving the pre-tension, thermo-infiltration of the rare earth element Ce, solution treatment, and artificial aging technology. The results indicate that the infiltration of rare earth element Ce benefits the abatement of anisotropy of Al-Li alloy 2195 sheet, in contrast with that of the normal heat treatment process. The gradient of the Vickers-hardness decreases at least 50% through the thickness, and the tensile strength in the rolling direction also increases significantly. If Ce was infiltrated into the alloy under the optimum pre-deformation, the yield strength （σ0.2） increased by 30 MPa while the tensile strength （σb） enhanced by 25 MPa compared to the rare earth free samples. Meanwhile, the fractography illustrated that the fracture surface of the sample became more desirable.
For the purpose of decreasing the applied limitation resulting from the anisotropic mechanical property of Al-Li alloy 2195, this study employed a complex heat treatment process, involving the pre-tension, thermo-infiltration of the rare earth element Ce, solution treatment, and artificial aging technology. The results indicate that the infiltration of rare earth element Ce benefits the abatement of anisotropy of Al-Li alloy 2195 sheet, in contrast with that of the normal heat treatment process. The gradient of the Vickers-hardness decreases at least 50% through the thickness, and the tensile strength in the rolling direction also increases significantly. If Ce was infiltrated into the alloy under the optimum pre-deformation, the yield strength （σ0.2） increased by 30 MPa while the tensile strength （σb） enhanced by 25 MPa compared to the rare earth free samples. Meanwhile, the fractography illustrated that the fracture surface of the sample became more desirable.
基金
Project supported by the National Key Laboratory of Precision Thermal Treatment , Harbin Institute of Technology(51471050105HK0101)