化学沉淀法制备CeO_2-La_2O_3-ZrO_2陶瓷粉末 被引量:8

Preparation of CeO_2-La_2O_3-ZrO_2 ceramic powder by chemical precipitation method
在线阅读 下载PDF
导出
摘要 采用化学沉淀法制备了La2Zr2O7(LZ)和CeO2-La2O3-ZrO2(LCZ)陶瓷粉末。通过电感耦合等离子体原子发射光谱(ICP-AES)、X射线衍射、DSC及霍尔流速计等分析方法,对粉末的化学组成、不同CeO2掺杂量LCZ的相组成、不同煅烧温度下的相组成、高温相稳定性和流动性能进行了研究。结果表明:所制备粉末的组成与锆酸镧烧绿石相的组成相近;热处理温度600℃时粉末为无定形的混合氧化物,900℃时转化为复合氧化物,1 150℃时转变为单一的锆酸镧烧绿石相;高温下LCZ无明显相变;温度高于1 400℃煅烧后,LCZ的流动性显著改善,可用于等离子喷涂。 Lanthanum zirconate (La2Zr2O7, LZ) and CeO2-La2O3-ZrO2 (LCZ) composite ceramic powders were prepared by the chemical precipitation. The chemical composition of the powders was analyzed by inductively coupled plasma-atomic emission spectrometry (ICP-AES). The crystallogrphic phases of LZ and LCZ with different CeO2 doped concentrations were determined by X-ray diffractometry. Differential scanning calorimetry (DSC) and TG were used to analyze the phase stability of LCZ sintered at different temperatures. The Hall flow meter was performed to determine the flowability of LCZ powder. The results show that the compositions of all prepared ceramic powders arc similar to that of La2Zr2O7 with pyrochlore structure, the ceramic powders are amorphous mixed oxide at 600 ℃, the amorphous mixed oxide is converted to composite oxide when temperature rises to 900 ℃, and the composite oxide is converted to single La2Zr2O7 with pyrochlore structure at 1 150℃. The LCZ powders keep pyrochlore structure and no phase transformations occur for LCZ at high temperatures (1 350 ℃). The flowability of LCZ powder sintered at 1 400 ℃ is improved clearly, and which could be used in plasma spray coatings.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2007年第2期265-269,共5页 The Chinese Journal of Nonferrous Metals
基金 中南大学博士后基金资助项目(76132017)
关键词 锆酸镧 复合陶瓷 热障涂层 化学沉淀法 lanthanum zirconate composite ceramics thermal barrier coatings chemical precipitation
  • 相关文献

参考文献15

  • 1Uwe S,Christoph L,Klaus F.Some recent trends in research and technology of advanced thermal barrier coatings[J].Aerospace Science and Technology,2003,7:73-80.
  • 2林锋,于月光,蒋显亮,曾克里,任先京,李振铎.等离子体喷涂纳米结构热障涂层微观组织及性能[J].中国有色金属学报,2006,16(3):482-487. 被引量:37
  • 3Sohn Y H,Lee E Y,Nagaraj B A.Microstructure characterization of thermal barrier coatings on high presser turbine blades[J].Surf Coat Technol,2001,146/147:132-137.
  • 4Chwa S O,Ohmori A.Microstructures of ZrO2-8 wt.% Y2O3 coatings prepared by a plasma laser hybrid spraying technique[J].Surf Coat Technol,2002,153:304-308.
  • 5Brandon J R,Taylor R.Phase stability of zirconia-based thermal barrier coatings(Part Ⅱ).Zirconia-ceria alloys[J].Surf Coat Technol,1991,46(1):91-96.
  • 6David R C,Simon R P.Thermal barrier coating materials[J].Materials Today,2005,6:22-29.
  • 7Wu J,Wei X Z,Padture N P,Klemens P G,Gell M,Garcia E.Low-thermal-conductivity rare-earth zirconates for potential thermal-barrier-coating applications[J].J Am Ceram Soc,2002,85(12):3031-3036.
  • 8Dietrich M,Vassen R,Stover D.LaYbO3,a candidate for thermal barrier coating materials[J].Ceram Eng Sci Proc,2003,24(3):637-643.
  • 9David R C.Materials selection guidelines for low thermal conductivity thermal barrier coatings[J].Surf Coat Technol,2003,163/164:67-74.
  • 10Vassen R,Cao X Q,Tietz F,Basu D,Stoever D.Zirconates as new materials for thermal barrier coating[J].Journal of the American Ceramic Society,2000,83(8):2023-2028.

二级参考文献24

  • 1[1]Miller R A, Smialek J L, Garlick R G. Phase stability in plasma sprayed partially stabilized zirconia-yttia. Advances in ceramics [A]. Heuer A H, Hobbs L W. Science and Technology of Zirconia (Vol.3) [C]. Columbus: American Ceramic Society, 1981
  • 2[2]Sohn Y H, Lee E Y, Nagaraj B A, et al. Microstructure characterization of thermal barrier coatings on high presser turbine blades [J]. Surf Coat Technol, 2001, 146-147:132
  • 3[3]Vassen R, Cao X Q, Tietz F, et al. Zirconates as new materials for thermal barrier coatings [J]. J Am Ceram Soc,2000, 83(8): 2023
  • 4[4]竹田博光.陶瓷镀层[M].康永林,王克智,译.香港:思远出版社,1993.201
  • 5[5]Roth R S, Negas T, Cook L P. Phase diagrams for ceramists [A]. Smith G. Science and Technology of Zirconia (Vol.4) [C]. Columbus: American Ceramic Society, 1981
  • 6[6]Subramanian A, Aravamudan G, Subba Rao G V. Oxide pyrochlores - a review [J]. Prog Solid State Chem, 1983,15:55
  • 7Gell M. Application opportunities for nanostructured materials and coatings[J]. Mater Sci Eng A, 1995,A204(4):246 - 251.
  • 8Chen X, Wang R, Yao N, et al. Foreign object damage in a thermal barrier system: mechanism and simulations[J]. Mater Sci Eng A, 2003, A325(1 - 2):221 - 231.
  • 9Watonabe M, Mercer C, Levi C G, et al. A probe for the high temperature deformation of thermal barrier oxides[J]. Acta Mater, 2004, 52(5): 1479-1487.
  • 10Lima R S, Kucuk A, Berndt C C. Evaluation of microhardness and elastic modulus of thermally sprayed nanostructured zirconia coatings [ J ]. Surface and Coatings Technology, 2001, 135(2) : 166 - 172.

共引文献56

同被引文献122

引证文献8

二级引证文献82

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部