Silver-tin oxide powders were synthesized by the hydrothermal method with Ag(NH_3)_2^+ solution and Na_2SnO_3 solution as raw materials and Na_2SO_3 as reductant. The precipitation conditions of Na2SnO3 solution and the reduction conditions of Ag(NH_3)_2^+ were also investigated. The powders prepared were characterized by differential thermal analysis (DTA), X-ray diffraction analysis (XRD), scanning electron microscope (SEM) and energy spectrum analysis. The results show that pH value of the solution is a key parameter in the formation of Sn(OH)_4 precipitate and the reduction reaction of Ag(NH_3)_2^+ can release H+ ions, which results in synchronous precipitation of Sn(OH)_6~2- as Sn(OH)_4. The reduction of Ag(NH_3)_2^+ and precipitation of Na_2SnO_3 occur simultaneously and the coprecipitation of silver and tin oxide is reached by the hydrothermal method. The silver-tin oxide composite powders have mainly flake shape of about 0.3 μm in thickness and there exists homogeneous distribution of tin oxide and silver in the powder synthesized.
Silver-tin oxide powders were synthesized by the hydrothermal method with Ag（NH3）2^＋ solution and Na2SnO3 solution as raw materials and Na2SO3 as reductant. The precipitation conditions of Na2SnO3 solution and the reduction conditions of Ag（NH3）2^＋ were also investigated. The powders prepared were characterized by differential thermal analysis （DTA）, X-ray diffraction analysis （XRD）, scanning electron microscope （SEM） and energy spectrum analysis, The results show that pH value of the solution is a key parameter in the formation of Sn（OH）4 precipitate and the reduction reaction of Ag（NH3）2^＋ can release H^＋ ions, which results in synchronous precipitation of Sn（OH）6^2- as Sn（OH）4. The reduction of Ag（NH3）2^＋ and precipitation of Na2SnO3 occur simultaneously and the coprecipitation of silver and tin oxide is reached by the hydrothermal method. The silver-tin oxide composite powders have mainly flake shape of about 0.3 μm in thickness and there exists homogeneous distribution of tin oxide and silver in the powder synthesized.
基金
Project(2001BA901A09)supported by the Key Program of Science and Technology Action of West China Development