Sr2SiO4：xEu^2＋ phosphors were synthesized through the solid-state reaction technique. The crystal phase of Sr2SiO4：xEu^2＋ phosphor manipulated by Eu^2＋ concentration was studied. The phase transited from β to α＇ in Sr2SiO4：xEu^2＋ phosphor with increasing europium concentration. The single β phase was formed as x≤005 and changed α＇ phase when x〉0.01. The emission spectrum of the β-Sr2SiO4：Eu^2＋ phosphor consisted of a green-yellow broadband peaking at around 540 nm and a blue band at 470 nm under near ultraviolet excitation. The white LEDs by combining near ultraviolet chips with β-Sr2SiO4：Eu^2＋ phosphors were fabricated. The luminous efficiency （15.7lm/W） was higher than α＇-Sr2SiO4：Eu^2＋ phosphor white LED.
Sr2SiO4：xEu^2＋ phosphors were synthesized through the solid-state reaction technique. The crystal phase of Sr2SiO4：xEu^2＋ phosphor manipulated by Eu^2＋ concentration was studied. The phase transited from β to α＇ in Sr2SiO4：xEu^2＋ phosphor with increasing europium concentration. The single β phase was formed as x≤005 and changed α＇ phase when x〉0.01. The emission spectrum of the β-Sr2SiO4：Eu^2＋ phosphor consisted of a green-yellow broadband peaking at around 540 nm and a blue band at 470 nm under near ultraviolet excitation. The white LEDs by combining near ultraviolet chips with β-Sr2SiO4：Eu^2＋ phosphors were fabricated. The luminous efficiency （15.7lm/W） was higher than α＇-Sr2SiO4：Eu^2＋ phosphor white LED.
基金
the Ministry of Science and Technology (MOST) of China (2006AA03A138)
the National Natural Science Foundation of China (10774141, 10574128)