摘要
为了提高血管支架的力学性能,将生物相容性良好的新型生物材料类人胶原蛋白(基因工程技术、高密度发酵生产)与丝素蛋白以质量比9:1、7:3、5:5复合,采用真空冷冻方法制备管状血管支架。研究了不同配比血管支架材料的表面结构、表面元素组成、力学性能、降解和生物相容性。结果表明:当类人胶原蛋白与丝素蛋白的质量比为7:3混合时,类人胶原蛋白-丝素蛋白管状支架具有均匀的多孔结构,孔径为(60±5)μm,孔隙率达到85%以上;获得了较理想的力学性能:应变为50%±5%,应力为(332±16)kPa;具有相对慢的降解速率;提高了细胞的黏附与增殖,具有良好的生物相容性。
In order to improve tensile property of vascular scaffold,we blended silk fibroin with novel human-like collagen with the mass ratio of 9：1,7：3 and 5：5（W/W）,and then fabricated blood vessel tubular graft by freeze-drying process.We studied microstructure,mechanical properties,elements composites,degradability and biocompatibility of vascular scaffolds.These results showed that tubular scaffold with mass ratio 7：3 exhibited interconnected porous structure with pore size at（60 ± 5） μm and porosity of 85%; achieved the desirable mechanical property （strain of 50%±5% and stress of 332±16 kPa）; had relatively slow degradation rate; could enhance cell adhesion and proliferation and had superior biocompatibility.
出处
《生物工程学报》
CAS
CSCD
北大核心
2009年第8期1225-1233,共9页
Chinese Journal of Biotechnology
基金
国家自然科学基金项目(No.20776119)
国家高技术研究发展计划(863计划)(No.2006AA02Z246)
陕西省教育厅专项科研计划项目(No.08JK452)
西安市科技计划项目(No.YF07078)资助~~