摘要
采用溶胶-凝胶法制备了钙钛矿型复合氧化物LaCoO3,并用沉积-沉淀法(DP法)制备了Au/LaCoO3催化剂.考察了制备条件对催化剂催化氧化CO活性的影响.结果表明,制备过程中,溶液pH、pH调节顺序及催化剂焙烧温度对催化剂活性均有一定影响.Au/LaCoO3催化剂的最佳制备条件为:沉积过程中在HAuCl4溶液中先加入载体后,再调节溶液pH=8,得到的催化剂经250℃焙烧后可提高催化剂稳定性.
Perovskite Oxide LaCoO3 were prepared by sol-gel method, then Au/LaCoO3 catalyst was prepared by deposition-precipitation method. The catalytic performance for CO low-temperature oxidation over this catalyst was investigated. The results showed the solution pH, the adjusting order of pH value and calcination temperature had different effect on catalyst activity. The optimal preparation condition for Au/LaCoO3 is as following： the support was firstly added to the precursor solution HAuCl4 , then pH was adjusted to 8. Calcination at 250℃ decreased the activity while improved the stability of catalyst.