摘要
通过差热分析曲线分析,5A12铝合金在实验条件下的低熔点共晶熔化温度不明显。在Gleeble-1500D上进行等温压缩实验,得到不同热变形条件下,合金宏观裂纹的变化情况。
The results of differential thermal analysis showed that the eutectic melting temperature of 5A12 aluminum alloy was not obvious under the experiment condition.The change of the macrocracks of the alloy was obtained under various conditions by isothermal compression test conducted on Gleeble-1500D.
出处
《铝加工》
CAS
2010年第1期34-36,共3页
Aluminium Fabrication