摘要
试验研究了Cu对高淬透性塑料模具钢淬透性的影响。结果表明:含铜和不含铜的试验钢都具有高淬透性;其中不含铜的T1钢奥氏体化后在冷速为0.03℃/s条件下,出现屈氏体;其它元素含量基本相同的含铜T2钢具有比T1更高的淬透性,在冷速为0.01℃/s条件下即能获得全马氏体。研究表明:Cu的添加可明显抑制奥氏体高温冷却过程向铁素体、珠光体的相变。
The effect of Cu on the hardenability of plastic mould steel with high hardenability was studied. The results showed that both the free Cu TI steel and T2 steel containing Cu owned the high hardenability. There were troostite appeared in T1 steel when cooling rate was 0.03℃/s. T2 steel had the lower C, Si, Mn, and Mo contents than that of T1 steel but showed a higher hardenabili- ty than T1 steel. There was martensite completely in T2 steel on the condition of 0.01 ℃/s cooling speed that meant the addition of Cu could inhibit the high temperature transformation strongly.
出处
《上海金属》
CAS
2010年第3期15-19,共5页
Shanghai Metals
基金
十一五国家科技支撑项目2007BAE51B04
关键词
含铜模具钢
高温冷却相变
淬透性
Copper Mould Steel, High Temperature Cooling Transformation, Hardenability