摘要
用电化学法制备了高度有序的多孔阳极氧化铝模板,选用CoSO4溶液为电解液,用交流电化学沉积法在多孔阳极氧化铝的柱形微孔内制备含钴纳米线有序阵列。分别用扫描电镜(SEM)、X射线衍射仪对多孔阳极氧化铝模板和纳米线阵列的微观形貌和结构进行分析,结果显示阳极氧化铝膜内确有钴生成,且钴纳米线中的晶粒在生长过程中有(100)晶面的择优取向。搭建了磁致偏振特性测试系统,对样品在大范围磁场下的退偏现象进行了测试。结果表明,含钴阳极氧化铝膜具有磁致偏光效应,达到磁饱和或接近磁饱和时,样品的的偏振性能最优,随着磁场的增强,出现了磁致退偏效应,并根据实验结果分析了磁致退偏效应的产生机理。
Highly ordered porous anodic aluminum oxide（PAA） membranes are prepared by electrochemical method.By alternating current electrodepositing,Co nanowire arrays are fabricated in the porous anodic alumina（PAA） in an electrolyte CoSO4.The morphology and microstructures of Co/PAA are characterized by SEM and X-ray diffraction.The results show that Co nanowires are indeed synthesized in porous alumina,and the nanowires have a preferred crystal face（100） during growing.The optical system is established in which the changes of polarization state for sample can be measured.In this optical system,the depolarization effect in Co/PAA which often be used in optical isolator is measured in large variation range of adjustable magnetic field.The experiment result shows that Co/PAA has depolarization effect in adjustable magnetic field,and the polarization performance is best in Co/PAA when it reaches saturated magnetization.The depolarization effect is occured when the intensity of magnetic field increases over saturation intensity.The principle for magnetic depolarization effect is also given according to the experimental result.
出处
《光学学报》
EI
CAS
CSCD
北大核心
2011年第1期266-271,共6页
Acta Optica Sinica
基金
国家自然科学基金(10947108)
山东省自然科学基金(Q2008A05)资助课题
关键词
薄膜
多孔阳极氧化铝
纳米线阵列
磁致偏光
退偏度
thin film
porous anodic alumina（PAA）
nanowire array
magnetic polarization
depolarization ratio