利用二次阳极氧化法在室温条件下制备了多孔氧化铝薄膜.采用扫描电镜、能量色散谱和X射线衍射对空气环境中600℃退火处理的多孔氧化铝薄膜进行了表面形貌、成分和结晶形式分析,结果表明多孔氧化铝薄膜孔阵排列有序、孔径大小一致,含有微量的C元素且为非晶态结构.在340nm的光激发条件下,多孔氧化铝薄膜出现峰值位于470nm的蓝绿发光带.通过分析得出,此光致发光带与草酸根离子发光基团有关.
Porous alumina film was fabricated in oxalic acid electrolyte by a two-step anodization method at room temperature. The film was annealed at 600% in the air. The surface morphology and crystalline state of the annealed film were investigated by scanning electron microscopy and X-ray diffraction, respectively. The constituent elements on the film surface were determined by Energy Disperse Spectroscopy. The results showed that the film was amorphous and presented highly ordered structures with uniform pore distribu- tion, and included trace carbon. The film presented a blue-green emission band at 470nm when it was excited at 340nm. We find that the origin of the emission band was related to the Oxalate luminophore.
出处
《新疆大学学报（自然科学版）》
CAS
2011年第2期222-225,共4页
Journal of Xinjiang University(Natural Science Edition)
基金
国家自然科学基金资助项目(No.10665002)
关键词
多孔氧化铝薄膜
二次阳极氧化法
光致发光
porous alumina film
two-step anodization method
Photoluminescence