摘要 Inconel 718 superalloys deposited by laser solid forming (LSF) were heat treated with solution treatment,intermediate heat treatment (IHT) and two-stage aging treatment in sequence (SITA heat treatment).The effect of IHT temperature on microstructure,tensile property and notch sensitivity of LSFed Inconel 718 superalloy at 500 ℃ were investigated.As-deposited columnar grains have transformed to equiaxed grains and the grains were refined due to the recrystallization during the SITA heat treatment.It is found that the size and amount of δ phase dispersed at grain boundaries decreased with the increasing of IHT temperature,and δ phase disappeared when the IHT temperature reached 1 020 ℃.The ultimate tensile strength (UTS) and yield strength (YS) of smooth samples increased to a maximum when the IHT temperature reached 980 ℃ and then decreased slightly to a minimum when the IHT temperature was 1 000 ℃,and followed by slight increasing again till the IHT temperature reached 1 020 ℃,resulted from the competition of precipitation strengthening effect of γ″ and γ' phase and the grain boundary weakening effect caused by the gradual disappearance of δ phase with increasing the IHT temperature.The notch sensitivity factor (qe) decreased but still greater than 1 as the IHT temperature increased,which is attributed to the decrease of the size and amount of δ precipitation. Inconel 718 superalloys deposited by laser solid forming (LSF) were heat treated with solution treatment,intermediate heat treatment (IHT) and two-stage aging treatment in sequence (SITA heat treatment).The effect of IHT temperature on microstructure,tensile property and notch sensitivity of LSFed Inconel 718 superalloy at 500 ℃ were investigated.As-deposited columnar grains have transformed to equiaxed grains and the grains were refined due to the recrystallization during the SITA heat treatment.It is found that the size and amount of δ phase dispersed at grain boundaries decreased with the increasing of IHT temperature,and δ phase disappeared when the IHT temperature reached 1 020 ℃.The ultimate tensile strength (UTS) and yield strength (YS) of smooth samples increased to a maximum when the IHT temperature reached 980 ℃ and then decreased slightly to a minimum when the IHT temperature was 1 000 ℃,and followed by slight increasing again till the IHT temperature reached 1 020 ℃,resulted from the competition of precipitation strengthening effect of γ″ and γ' phase and the grain boundary weakening effect caused by the gradual disappearance of δ phase with increasing the IHT temperature.The notch sensitivity factor (qe) decreased but still greater than 1 as the IHT temperature increased,which is attributed to the decrease of the size and amount of δ precipitation.
出处 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2011年第5期908-913,共6页 武汉理工大学学报(材料科学英文版)
基金 Funded by the Program for New Century Excellent Talents in University of China (No.NCET-06-0879) the National Natural Science Foundation of China (NSFC) (No.50971102) NPU Foundation for Fundamental Research(No.NPU-FFR-JC200808) the Fund of the State Key Laboratory of Solidification Processing (NPU) (Nos.16-TZ-2007 and 39-QZ-2009) supported by the Program of Introducing Talents of Discipline to Universities (No.08040)
关键词 notch sensitivity Inconel 718 laser solid forming intermediate heat treatment SUPERALLOY notch sensitivity Inconel 718 laser solid forming intermediate heat treatment superalloy
  • 相关文献

参考文献1

二级参考文献27

  • 1Lewis G K, Nemec R B, Milewski J O, Thoma D L, Barbe M R, Cremers D A. In: Proc ICALEO '94. Orlando:Laser Institute of America, 1994:17.
  • 2Keicher D M, Smugeresky J E, Romero J A, Griifith M L,Harwell L D. Proc SPIE, 1997, 2993:91.
  • 3Schlienger E, Dimos D, Griffith M, Michael J, Oliver M,Romero T, Smugeresky J. In: Proc 3rd Pacific Rim Int Conf on Advanced Materials and Processing, Vol I. Warrandale: TMS, 1998:1581.
  • 4Mazumder J, Schitferer A, Choi J. Mater Res Innovat,1999, 3:118.
  • 5Link G R, Fessler J, Nickel A, Prinz F. Mater Manuf Process, 1992, 13:263.
  • 6Gaumann M, Henry S, Cleton F, Wagniere J D, Kurz W.Mater Sci Eng, 1999, A271:232.
  • 7Li Y M, Yang H O, Lin X, Huang W D, Li J G, Zhou Y H. Mater Sci Eng, 2003, A360:18.
  • 8张长利.北京航空航天大学硕士学位论文.2002.
  • 9Zhang Y Z,Xi M Z,Gao S Y,Shi L K.J Mate Proc Technol,2003,142:582.
  • 10Zhong M L, Liu W J, Ning G G, Yang L, Chen Y X. J Mater Process Technol, 2004, 147:167.

共引文献74

同被引文献71

引证文献4

二级引证文献63

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部