摘要
针对某油气田地面工程复合管一次焊接合格率低的问题,从焊接工艺、缺陷产生机理、操作规范等方面分析缺陷产生的原因。指出封焊层质量失控、过渡层焊接操作不当是造成气孔、未熔合等缺陷产生的原因。结果表明,加强关键工序的质量控制,改进焊接操作方法,对提高一次焊接合格率是有效的。
In view of the problem of the low primary welding qualified rate about the composite pipes of ground engineering in an oil-gas field,this article analyzes the causes of defects from the aspects of welding process,the mechanism of defect occurrence,and the operating regulation.It is pointed out that defects such as blowhole,incomplete fusion are caused by being out of control in the quality of seal welding layer and the improper operation of transition welding layer.The results show that enhancing the quality control of key technological process and improving the method of welding operation are effective in improving the primary qualified rate of welding.
出处
《石油工业技术监督》
2011年第10期18-20,共3页
Technology Supervision in Petroleum Industry
关键词
复合管
焊接
缺陷
质量控制
composite pipe
welding
defect
quality control