摘要
The microstructure,tensile properties at 20—950℃ and creep rupture properties at 700- 900℃ in a Ni_3Al-Fe based alloy after high temperature deformation have been studied.The results show the microstructure of the alloy is composed of γ′-and β-phases.The grain size and yield strength of the alloy is stable when the temperature≤600℃,and it is ductile at high temperature.The creep of the alloy at 700—900℃ is controlled by the climbing of dislo- cations,and the activation energy for creep is 439 KJ/mol with a stress exponent of 4.
The microstructure,tensile properties at 20—950℃ and creep rupture properties at 700- 900℃ in a Ni_3Al-Fe based alloy after high temperature deformation have been studied.The results show the microstructure of the alloy is composed of γ′-and β-phases.The grain size and yield strength of the alloy is stable when the temperature≤600℃,and it is ductile at high temperature.The creep of the alloy at 700—900℃ is controlled by the climbing of dislo- cations,and the activation energy for creep is 439 KJ/mol with a stress exponent of 4.