This work investigated the microwave dielectric properties of A-site substitution by rare earth La3＋in（Pb0.5Ca0.5）（Fe0.5Ta0.5）O3（PCFT） system.A single perovskite phase was obtained only when the doping content was 2%.Suitable La3＋ doping improved microwave dielectric performances.Excessive La3＋doping caused the formation of secondary phase,which resulted in the decreasing of permittivity εrand quality factor Qfvalues.Especially,when the doping content is 2%-5%,permittivity εrwas above 75 and Qfvalues were 6 902-7 416 GHz.
This work investigated the microwave dielectric properties of A-site substitution by rare earth La3＋in（Pb0.5Ca0.5）（Fe0.5Ta0.5）O3（PCFT） system.A single perovskite phase was obtained only when the doping content was 2%.Suitable La3＋ doping improved microwave dielectric performances.Excessive La3＋doping caused the formation of secondary phase,which resulted in the decreasing of permittivity εrand quality factor Qfvalues.Especially,when the doping content is 2%-5%,permittivity εrwas above 75 and Qfvalues were 6 902-7 416 GHz.
基金
Project supported by the National Natural Science Foundation of China (Grant No.60578041)
the National High Technology Research and Development Program of China (Grant No.715-006-0060)