摘要
Effects of cold rolling on the microstructure and mechanical properties of Fe-Ni-Mn-Mo-Ti-Cr maraging steels were studied.To investigate the microstructure and mechanical properties,optical microscopy,scanning electron microscopy,X-ray diffraction,tensile test,and hardness test were used.The results show that the solution-annealing treatment in the cold-rolled steel redounds to the formation of sub-microcrystalline Fe2（Mo,Ti） Laves phase particles,which are stable at high temperatures.These secondary Laves phase particles prevent from recrystallization at high temperatures and correspond to semi-brittle fracture in the subsequent aging treatment.
Effects of cold rolling on the microstructure and mechanical properties of Fe-Ni-Mn-Mo-Ti-Cr maraging steels were studied.To investigate the microstructure and mechanical properties,optical microscopy,scanning electron microscopy,X-ray diffraction,tensile test,and hardness test were used.The results show that the solution-annealing treatment in the cold-rolled steel redounds to the formation of sub-microcrystalline Fe2（Mo,Ti） Laves phase particles,which are stable at high temperatures.These secondary Laves phase particles prevent from recrystallization at high temperatures and correspond to semi-brittle fracture in the subsequent aging treatment.