Lap joints of TC1 Ti alloy and LF6 A1 alloy dissimilar materials were fabricated by friction stir welding and corresponding interface characteristics were investigated. Using the selected welding parameters, excellent surface appearance forms, but the interface macrograph for each lap joint cross-section is different. With the increase of welding speed or the decrease of tool rotation rate, the amount of Ti alloy particles stirred into the stir zone by the force of tool pin decreases continuously. Moreover, the failure loads of the lap joints also decrease with increasing welding speed and the largest value is achieved at welding speed of 60 mm/min and tool rotation rate of 1500 r/min, where the interracial zone can be divided into 3 kinds of layers. The microhardness of the lap joint shows an uneven distribution and the maximum hardness of HV 502 is found in the middle of the stir zone.
采用搅拌摩擦焊实现TC1钛合金和LF6铝合金异种材料的搭接连接,并对界面特性进行研究。采用所选取的工艺参数均能获得良好的表面成形,但每一种工艺参数下的界面形貌不同。随着焊接速度的增加或搅拌头转速的降低,被搅拌针搅入焊核区的钛合金粒子的数量减少,而且搭接接头的抗拉载荷也随着焊接速度的提高而降低。当焊接速度为60mm/min、搅拌头旋转速度为1500r/min时,接头的抗拉载荷达到最大值,此时的界面区可以分成三层。搭接接头的显微硬度分布不均匀,焊核中心区的显微硬度值最大,高达HV502。
基金
Project (2011BAB206006) supported by the Natural Science Foundation of Jiangxi Province,China
Project (2009ZE56011) supported by the Aviation Science Funds of China
Project (GJJ12411) supported by the Education Department of Jiangxi Province,China