摘要
针对351nm激光诱导熔石英样品进行损伤实验。采用激光近场辐照样品,并基于近场辐照的损伤阈值定义方法进行损伤测试。利用带有灰度抑制的分水岭标记分割算法对损伤图像进行损伤区域提取,与相应近场分布进行比较,得到损伤区域边界点对应的局域能量密度即为损伤阈值。这种损伤测试方法简单、快速,有效降低了损伤阈值口径效应,且采用了能够有效去除噪声和抑制图像过分割问题的算法对损伤图像进行处理,使得到的损伤阈值和损伤增长系数有较高的准确性。实验结果表明,脉冲宽度为3.13ns的351nm激光诱导熔石英样品的损伤阈值为2.94J/cm2;在多次辐照样品情况下,熔石英样品出射面的损伤尺寸随着辐照次数的增加呈指数增长,其损伤增长系数为0.32。
Damage experiments are conducted by irradiating 351 nm laser near-filed to fused silica based on the damage threshold definition of near-filed irradiating. Damage areas are extracted from damage images by the marker- based watershed algorithm with gray control. The initial damage threshold is defined as the fluence of critical site between damage region and no damage region, which is calculated by comparing the damage image with 351nm laser near-field. This damage testing method is sample, quick, which can effectively decrease the effect of beam diameter for damage threshold due to the bigger aperture. The algorithm of image segmentation effectively removes the noise and suppresses the over-segmentation, and improves the accuracy of initial damage and damage growth. The research shows that the damage of fused silica is induced by 351 nm laser near-field with pulse width of 3.13 ns. The initial damage threshold is 2. 94 J/cm2. With multiple irradiation of fused silica, the damage growth of exit surface is exponential, and the coefficient of damage growth is 0.32.
出处
《中国激光》
EI
CAS
CSCD
北大核心
2013年第5期19-23,共5页
Chinese Journal of Lasers