Balance solubility products and enthalpy of for- mation for NbC0.75, NbC0.85, NbC0.88, NbC and NbN in oriented silicon steels were calculated and compared quali- tatively. Meanwhile, the mixing enthalpies of these five Nb compounds were calculated based on Miedema Model. The results show that the solubility products of Nb compounds in ferrite and austenite meet the following relationship, NbC0.75 〉 NbC0.85 〉 NbC0.88 〉 NbC 〉 NbN and NbN has the minimum enthalpy of formation. It indicates that NbN easily precipitate out, but it is more difficult for NbC0.75.
Balance solubility products and enthalpy of for- mation for NbC0.75, NbC0.85, NbC0.88, NbC and NbN in oriented silicon steels were calculated and compared quali- tatively. Meanwhile, the mixing enthalpies of these five Nb compounds were calculated based on Miedema Model. The results show that the solubility products of Nb compounds in ferrite and austenite meet the following relationship, NbC0.75 〉 NbC0.85 〉 NbC0.88 〉 NbC 〉 NbN and NbN has the minimum enthalpy of formation. It indicates that NbN easily precipitate out, but it is more difficult for NbC0.75.
基金
financially supported by the National Natural Science Foundation of China (Nos. 51274083 and 51074062)