摘要
利用溶胶-凝胶和溶剂热联合技术制备了Pr-N-P三元掺杂锐钛矿TiO2(PrNPTO)纳米片,并采用X射线衍射、透射电镜、N2吸附、X射线光电子能谱、UV-vis吸收谱和光致荧光光谱分析技术对其进行了表征.当Pr掺杂量为1.75 wt%,焙烧温度为550°C时,制得的PrNPTO在可见和紫外光下光催化降解亚甲基蓝(MB)活性最佳.在模拟太阳光照射下,PrNPTO也表现出优越的光催化降解4-氯酚性能(kapp=3.90×10-2 min-1),优于未掺杂、单掺杂和双掺杂TiO2样品,其光活性是P25 TiO2的3.33倍(kapp=1.17×10-2min-1).PrNPTO光活性的提高归因于Pr-N-P三元掺杂增强了紫外和可见光吸收,降低了光生载流子复合,增加了表面羟基以及改善了表面织构特性.在模拟太阳光照射下,PrNPTO光催化效率高且光催化性能稳定,适合于环境净化领域的实际应用..
Pr, N, and P tri-doped anatase TiO2 nanosheets （PrNPTO） were synthesized by a combined sol-gel solvothermal method and characterized by X-ray diffraction, transmission electron microscopy, N2 adsorption-desorption, X-ray photoelectron spectroscopy, UV-vis absorbance spectroscopy, and photoluminescence spectroscopy. When the Pr-doping concentration was 1.75 wt% and calcination temperature employed was 550 ℃, the resulting PrNPTO showed the highest photoactivity towards the degradation of methylene blue under visible and UV light irradiation. PrNPTO also displayed superior photoactivity towards the degradation of 4-chlorophenol under sunlight （kapp = 3.90 × 10^-2 min^-1） over the non-doped, single-doped, and co-doped samples, and P25 TiO2 （kapp = 1.17 × 10^-2 min^-1）. The high photoactivity of PrNPTO was attributed to the increased UV and visible light absorption properties, reduced recombination of photogenerated carriers, increased surface hydroxyl content, and improved surface textural properties. PrNPTO was highly efficient and stable under simulated sunlight irradiation, which are essential attributes for practical application in environment-related remediation schemes.
出处
《催化学报》
SCIE
EI
CAS
CSCD
北大核心
2014年第7期1068-1077,共10页
基金
supported by the Natural Science Foundation of Heilongjiang Province (E201323)
the Harbin Special Fund for Innovation Talents of Science and Technology (2013RFXXJ081)
the Science and Technology Research Program of Education Bureau of Heilongjiang Province (12531213)~~