摘要
矿物聚合材料是以铝硅酸盐矿物或工业固体废物为主要原料制备而成的一类新型无机非金属材料。实验对利用铝质岩、石英砂、高岭土、氢氧化钠和水玻璃制备矿物聚合材料进行探索性研究,对影响材料力学性能的主要因素进行分析。结果表明:高岭土在750℃下煅烧6 h,H0的加入量占液相8%,Ca(OH)2占2%,石英砂占23.61%,高岭土占26.92%,水玻璃占液相的50%。固液比为2.2,在此条件下,聚合物的抗压强度达到最大值32.78 MPa。
Geopolymers is a new type inorganic non-metallic material that taking alumino-silicate source or industrial solid wastes as main materials. Exploratory tests using Aluminous rock,quartz sand,kaolin clay,sodium hydroxide and water glass and analyzed main factors the mechanical property of Geopolymers. Experimental results show that the compressive strength of Geopolymers is 32. 782 MPa.The best experimental conditions were Kaolin calcined 6 h under 750 ℃ temperature,2% Ca（ OH）2,the solid /liquid ratio was 2. 2,Alkali activator accounted for 8% of liquid-phase and sodium silicate occupied 50%.
出处
《硅酸盐通报》
CAS
CSCD
北大核心
2014年第9期2212-2216,2222,共6页
Bulletin of the Chinese Ceramic Society
基金
贵州省科技厅工业公关项目(黔科合GY[2012]3055)
贵州省教育厅培育项目(20090131)
贵州省科技厅国际合作项目([2010]007)
国家自然科学基金(51164004)
关键词
矿物聚合物
抗压强度
物理化学特征
geopolymers
gompressive strength
physical-chemical property