摘要
An A1203p/A1 composite was successfully synthesized using a displacement reaction between 80 wt% A1 and 20 wt% CuO powders at a heating rate of 5 ℃/min. Two different sizes CuO particles were used, and all the experiments were conducted under an argon atmosphere. To analyze the microstructural evolution during synthesis, the A1-20 wt% CuO samples were heated to the temperatures selected according to the differential scanning calorimetry curve and then immediately quenched with water. The phase composites and microstructure of the water-quenching samples were in- vestigated using X-ray diffraction, optical microscopy, scanning electron microscopy and energy-dispersive spectrometry. The results indicate that the CuO particle size has a significant effect on the microstructural evolution of the samples during the heating stage and on the microstructure of synthesized composites. Smaller CuO particles can decrease the reaction temperature, narrow the reaction temperature range at the different reaction stages during the heating stage and make the size and distribution of in situ A1203 particles more uniform. The reaction between A1 and CuO can be complete as the temperature rises to 900 ℃. The size of the in situ A1203 particles is approximately 5 μm when the size of the CuO particles is less than 6 μm. This sample has a relatively high Rockwell hardness of 60 HRB.
An A1203p/A1 composite was successfully synthesized using a displacement reaction between 80 wt% A1 and 20 wt% CuO powders at a heating rate of 5 ℃/min. Two different sizes CuO particles were used, and all the experiments were conducted under an argon atmosphere. To analyze the microstructural evolution during synthesis, the A1-20 wt% CuO samples were heated to the temperatures selected according to the differential scanning calorimetry curve and then immediately quenched with water. The phase composites and microstructure of the water-quenching samples were in- vestigated using X-ray diffraction, optical microscopy, scanning electron microscopy and energy-dispersive spectrometry. The results indicate that the CuO particle size has a significant effect on the microstructural evolution of the samples during the heating stage and on the microstructure of synthesized composites. Smaller CuO particles can decrease the reaction temperature, narrow the reaction temperature range at the different reaction stages during the heating stage and make the size and distribution of in situ A1203 particles more uniform. The reaction between A1 and CuO can be complete as the temperature rises to 900 ℃. The size of the in situ A1203 particles is approximately 5 μm when the size of the CuO particles is less than 6 μm. This sample has a relatively high Rockwell hardness of 60 HRB.
基金
financially supported by the Inner Mongolia Natural Science Foundation of China (Nos. 2012MS0801 and 2013MS0804)