以球状纳米Cu_2O为核心,直接牺牲其表面的部分Cu_2O,与溶液中的均苯三羧酸(H_3BTC)配体反应,原位生成具有核壳结构的Cu_2O@HKUST-1材料。采用O_2程序升温脱附(O_2-TPD)、H_2程序升温还原(H2-TPR)及CO氧化反应对Cu_2O@HKUST-1核壳材料的抗氧化能力进行了研究,证明金属-有机框架材料(MOFs)HKUST-1对反应气体起到富集、缓释作用,保护Cu_2O核不被氧化,显著提高了其抗氧化能力。
Spherical nanometer Cu2O was employed as the core with partial of whose Cu2O on surface sacrificing, which reacted with benzene-1,3,5-triearboxylic acid （H3BTC） ligand in solution, forming the product of CUEO@HKUST-1 with core-shell structure in situ. The antioxidant ability of core-shell-structure CUEO@HKUST-1 was investigated by O2 temperature programmed desorption （O2-TPD）, H2 temperature programmed reduction （H2- TPR） and CO oxidation reaction. The result shows that the Cu2O antioxidant ability is significantly increased. The metal-organic frameworks （MOFs） HKUST-1 could protect Cu2O from oxidation because of its enrichment and slow-release of reacting gas.
出处
《无机化学学报》
SCIE
CAS
CSCD
北大核心
2016年第7期1149-1153,共5页
Chinese Journal of Inorganic Chemistry
基金
国家自然科学基金(No.21561020
21261017)
江西省自然科学基金(No.20122BAB213003
20132BAB203009
20132BAB213004
20133ACB20001)
江西省教育厅自然科学基金(No.GJJ11012)资助项目