摘要
首次报道通过一种聚苯乙烯磺酸钠(PSS)和三嵌段共聚物(P123)辅助的水热法,以Ni(NO3)2为原料,合成了新颖的绒球状β-氢氧化镍微米球(P1),其结构和形貌经X-射线衍射、扫描电镜和透射电镜表征。电化学测试结果表明:P1具有良好的电化学性质,在1 A·g-1电流密度下,电容量达1 214 F·g-1,经过1 000次循环后其容量可保持90%以上。
The novel self-assembled pompon-like β-Ni （OH） 2 microspheres （ p1 ） was synthesized for the first time, by the hydrothermal reaction of Ni （NO3 ）2 with the assistance of sodium poly（4-styrene- sulfonate） （PSS） and triblock copolymer Pluronic （ P123 ） as the morphological controling suffactants. The structures and morphology were characterized by XRD, SEM and TEM. The electrochemical prop-erties of p1 were studied. The results showed that P1 exhibited excellent capacitance behavior with cou- lombic efficiency of 1 214 F·g^-1 at a charge/discharge current density of 1 A·g^-1 and an almost 90% coulombic efficiency after 1 000 cycles.
作者
刘正
LIU Zheng(Chengdu Jufeng Glass Co. , Ltd. , Chengdu 610300, China)
出处
《合成化学》
CAS
CSCD
2016年第10期861-865,共5页
Chinese Journal of Synthetic Chemistry
关键词
聚苯乙烯磺酸钠
三嵌段共聚物
水热法
绒球状β-氢氧化镍微米球
可控合成
电化学性质
超级电容器
sodium poly （4-styrenesulfonate）
triblock copolymer
hydrothermal method
pompon-like β-Ni （OH） 2 microsphere
controllabe synthesis
electrochemical property
supercapacitor