考察了均匀剂RH-150对天然橡胶(NR)/丁腈橡胶(NBR)共混胶硫化特性、物理机械性能、压缩生热及阻尼性能的影响。结果表明,随着均匀剂RH-150用量的增加,NR/NBR混炼胶的加工性能和操作安全性逐渐提高,拉伸强度和撕裂强度均先提高后降低,分别在RH-150用量为5份和8份时达到最大值,同时定伸应力和回弹性逐渐减小,扯断伸长率、疲劳温升和动态压缩永久变形均增大,阻尼性能提高。
The effects of the homogenizing agent（ RH-150） on the curing characteristics,mechanical properties,compression fatigue heat build-up and damping properties of natural rubber（ NR）/nitrile rubber（ NBR） blends were investigated.The results showed that the processability and operation safety of NR/NBR blends were gradually improved with the increase of the amount of RH-150. The tensile strength and tear strength increased first and then decreased, and tensile strength and tearing strength reached the maximum values when RH-150 was 5 phr and 8 phr respectively,while the modulus and rebound resilience decreased gradually,elongation at break,temperature rise and the dynamic compression permanent set increased gradually,and the damping properties were improved.
作者
王建功
梁世宗
任慧
魏继军
陈自安
薛美玲
WANG Jian-gong1, LIANG Shi-zong2 , REN Hui1, WEI Ji-jun1 , CHEN Zi-an1 , XUE Mei-ling1(1. College of Polymer Science and Engineering, Qingdao University of Science ＆ Technology, Qingdao 266042, China ;2. Trelleborg Engineered Systems （ Qingdao） Co Ltd, Qingdao 266111, China)
出处
《合成橡胶工业》
CAS
CSCD
北大核心
2018年第3期208-212,共5页
China Synthetic Rubber Industry
基金
国家自然科学基金资助项目(51673104
51173089)
山东省重点研发计划资助项目(2015 GGX102002)
关键词
天然橡胶
丁腈橡胶
均匀剂
物理机械性能
压缩生热
阻尼性能
natural rubber
nitrile rubber
homogenizing agent
mechanical property
compression fatigue heat build-up
damping property