半导体复合材料中的光生载流子动力学过程是影响其光催化性能的重要因素之一。该工作以二水合氯化亚锡(SnCl_2·2H_2O)为原料,NaOH为沉淀剂,采用一步溶剂热法制备了Sn的氧化物纳米SnO-SnO_2复合材料,并利用SEM、XRD、TEM和Uv-Vis光谱等对产物进行了表征。结果表明,通过控制反应条件可以获得粒径约为10～20nm的SnO-SnO_2复合材料和粒径约为10nm的四方相SnO_2颗粒,分散性较好。光催化性能研究表明,纳米SnO-SnO_2复合材料完全催化降解罗丹明B(RhB)的时间比纳米SnO_2颗粒减少50%。针对这一结果,利用瞬态表面光电压(TSPV)技术分别对上述纳米材料的光生载流子动力学过程进行了讨论。结果表明,纳米SnO-SnO_2复合结构的构建可以有效地促进光生载流子的分离,抑制SnO_2表面光生载流子的复合及提高材料表面的光生载流子的寿命,进而显著增强其光催化性能。
The photoinduced charge carrier dynamics is one of the important factors that affect the photocatalytic performace of semiconductor composites.In this work,tin oxides nano-particles were successfully fabricated by onestep solvent thermal method using SnCl2·2H2O as raw material and NaOH as precipitant.The fabricated samples were characterized by SEM,XRD,TEM and Uv-Vis spectra.The results show that about 10-20 nm particles size SnO-SnO2 composites and about 10 nm tetragonal SnO2 particles can be obtained by adjusting the reaction condition.Photocatalytic degradation performance of the above two nano-materials has been evaluated by using Rhodamine（RhB）as the degradation agent.The degradation time of RhB can be reduced by 50%by using nano SnO-SnO2 composites as photocatalyst compared with pure nano SnO2 particles.For further studying the mechanism for this result,transient surface photovoltage（TSPV）technique has been carried out to understand the photoinduced charge carrier dynamics of the resulting materials.The corresponding results show that the photoinduced charge carrier separation has been enhanced,the surface recombination of photoinduced charge carrier has been reduced,and the lifetime of photoinduced charge carrier on the material surface is prolonged by building the nano SnO-SnO2 composites.Finally,the consequent photocatalystic performance is enhanced.
作者
谷龙艳
杨健康
侯兴凯
铁伟伟
雷岩
郑直
GU Longyan; YANG Jiankang; HOU Xingkai; TIE Weiwei; LEI Yan; ZHENG Zhi(Key Laboratory of Micro-Nano Materials for Energy Storage and Conversion of He＇nan Province, Institute of Surface Micro and Nano Materials, School of Advanced Materials and Energy, Xuchang University, Xuchang 461000, China)
出处
《复合材料学报》
EI
CAS
CSCD
北大核心
2018年第10期2624-2631,共8页
Acta Materiae Compositae Sinica
基金
许昌学院科研项目(2018YB010)
许昌市科技攻关社会发展项目(20160213154)
国家自然科学基金(61504117
61605167)