在热模拟实验机上采用单道次压缩法对高强船板钢EH47在不同变形条件下的高温变形行为以及变形工艺参数对显微组织的影响进行了研究。结果表明:高强船板钢EH47在不同变形条件下的应力-应变曲线均为动态回复型。随着变形温度升高、变形速率降低,高强船板钢EH47的变形抗力减小。随着变形温度升高、变形速率降低,高强船板钢EH47的硬度减小。这实验结果与显微组织分析结果相一致。
The thermal deformation behavior under different deformation conditions and the effects of deformationprocess parameters on the microstructure of high strength hull steel EH47 were studied by using single channel compressionmethod in thermal simulation experiment. The results show that the stress - strain curves of high strength hull steel EH47 aredynamic recovery under different deformation conditions. With the increase of deformation temperature, the decrease ofdeformation rate, the deformation resistance of high strength hull steel EH47 decrease. With the increase of deformationtemperature and decrease of deformation rate, the hardness of high strength hull steel EH47 decreases. The experimentalresults are consistent with the results of microstructure analysis.
作者
朱阳阳
张红梅
贾宏斌
李岩
李娜
姜正义
ZHU Yangyang;ZHANG Hongmei;JIA Hongbin;LI Yan;LI Na;JIANG Zhengyi(School of Materials and Metallurgy,University of Science and Technology Liaoning,Anshan 114051,China;State Key Laboratory of Metal Material for Marine Equipment and Application,Anshan 114009,China;Large Section Profile Steel Rolling Mill,Angang Steel Company Limited,Anshan 114021,China)
出处
《热加工工艺》
北大核心
2019年第22期23-26,共4页
Hot Working Technology
基金
辽宁省自然科学基金指导计划(20180550952)
辽宁科技大学与海工钢国家重点实验室联合项目(SKLMEAUSTL2017010)
关键词
高强船板钢EH47
变形工艺参数
高温变形行为
显微组织
high strength hull steel EH47
deformation process parameters
high temperature deformation behavior
microstructure