摘要
A small amount of Ni was added into the binary Gd50Co50 amorphous alloy to replace Gd in order to obtain ternary Co50Gd50-xNx(x=1,2,and 3)amorphous alloys.Compared to the binary Gd50Co50 amorphous alloy,the Co50Gd50-xNx amorphous alloys show an enhanced Curie temperature(TC)with a weakened formability.The maximum magnetic entropy change(-Δ^Smpeak)of the Co50Gd50-xNx amorphous alloys is found to decrease with the increasing TC.The adiabatic temperature rise(ΔTad)of the Co50Gd47Ni3 amorphous alloy is superior to that of the Fe-based metallic glasses at room temperature.The variation of the TC and-Δ^Smpeak of the Gd50Co50 amorphous alloy with Ni addition,and the mechanism involved,were discussed.
作者
Ben-Zheng Tang
Xiao-Ping Liu
Dong-Mei Li
Peng Yu
Lei Xia
唐本镇;刘晓萍;李冬梅;余鹏;夏雷(Chongqing Key Laboratory of Photo-Electric Functional Materials,College of Physics and Electronic Engineering,Chongqing Normal University,Chongqing 401331,China;Laboratory for Microstructure&Institute of Materials,Shanghai University,Shanghai 200072,China)
基金
Project supported by the National Natural Science Foundation of China(Grant Nos.51671119 and 51871139)
the Chongqing Research Program of Basic Research and Frontier Technology,China(Grant No.cstc2018jcyjAX0329 and cstc2018jcyjAX0444)
the Key Project of Science and Technology Research Program of Chongqing Education Commission of China(Grant No.KJZD-K201900501).