摘要
The effect of the preparation method on the properties of LaMnO3 and La0.8Sr0.2MnO3 perovskite was studied. Materials were prepared by four methods: sol-gel, chemical combustion, solvothermal and spray pyrolysis and characterized. The effect of the synthesis method on the texture, acid-base character of the surface, reducibility with hydrogen, oxygen desorption, surface composition and catalytic activity for combustion of lean methane was studied. It was found that synthesis method affects physicochemical properties of obtained materials-solvothermally produced materials exhibit well-developed surface area, presence of reactive oxygen species on surface and high catalytic activity for CH4 combustion. Generally, LaMnO3 and La0.8Sr0.2MnO3 perovskites show catalytic activity for lean CH4 combustion comparable or higher than the activity of 0.5 wt.% Pt/Al2O3 but lower than 1 wt.% Pd/Al2O3.
The effect of the preparation method on the properties of LaMnO3 and La0.8Sr0.2MnO3 perovskite was studied. Materials were prepared by four methods: sol-gel, chemical combustion, solvothermal and spray pyrolysis and characterized. The effect of the synthesis method on the texture, acid-base character of the surface, reducibility with hydrogen, oxygen desorption, surface composition and catalytic activity for combustion of lean methane was studied. It was found that synthesis method affects physicochemical properties of obtained materials-solvothermally produced materials exhibit well-developed surface area, presence of reactive oxygen species on surface and high catalytic activity for CH4 combustion. Generally, LaMnO3 and La0.8Sr0.2MnO3 perovskites show catalytic activity for lean CH4 combustion comparable or higher than the activity of 0.5 wt.% Pt/Al2O3 but lower than 1 wt.% Pd/Al2O3.
基金
financed by a statutory activity subsidy from the Polish Ministry of Science and Higher Education for the Faculty of Chemistry of Wroclaw University of Technology.