BaCe0.45Zr0.45M0.1O3-δ （M=Y, In） and BaCe0.9Y0.1O3-δ were prepared through the conventional solid state reaction route. The chemical stability was investigated in hydrogen, carbon dioxide, and boiling water. Cryst...BaCe0.45Zr0.45M0.1O3-δ （M=Y, In） and BaCe0.9Y0.1O3-δ were prepared through the conventional solid state reaction route. The chemical stability was investigated in hydrogen, carbon dioxide, and boiling water. Crystalline phase and microsa-ucture of the proton conductor before and after stability test were measured with X-ray diffraction （XRD） and scanning electron microscopy （SEM）, respectively. The results showed that all materials were quite stable in H2 atmosphere. In CO2 atmosphere, BaCe0.45Zr0.45M0.1O3-δ（M=Y, In） were relatively stable, while Bafe0.9Y0.1O3-δ decomposed. In boiling water, BaCe0.9Y0.1O3-δ was quickly decomposed into Ba（OH）2 and corresponding oxide. BaCe0.45Zr0.45M0.1O3-δ slightly reacted with boiling water and some amorphous phases were formed. However, BaCe0.45Zr0.45In0.1O3-δ was observed to exhibit better stability than BaCe0.45Zr0.45Y0.1O3-δ in water. The experimental results were interpreted in terms of thermodynamic data and tolerance factor.展开更多
The support of catalyst for the direct synthesis of diphenyl carbonate （DPC） by heterogeneous catalytic reaction was prepared by the sol-gel method. Compared with activated charcoal, molecular sieve, porous ceramics...The support of catalyst for the direct synthesis of diphenyl carbonate （DPC） by heterogeneous catalytic reaction was prepared by the sol-gel method. Compared with activated charcoal, molecular sieve, porous ceramics, hopcalite, the support prepared by the sol-gel method has higher activity. The characterization of the support by X-ray diffraction （XRD） and transmission electron microscope （TEM） show that the mare crystal phase is Co2MnO4 and the average particle diameter is about 40 nm. The optimum conditions for synthesis of the support were determined by orthogonal experiments, which indicate that the proportion of Cu, Mn, and Co is the first important factor influencing the yield and selectivity of DPC. Temperature of calcination is the second one. The optimum conditions are： molar proportion of Cu, Mn, and Co being 1 ： 1 ： 1, temperature of calcination 700℃, drying at 100~C, temperature of water bath 85~C. The yield and selectivity of DPC in the process can reach 38% and 99% in the batch operation, respectively. The copper cobalt manganese mixed oxides chosen as the support contribute more to the high catalytic activity than the sol-gel method.展开更多
基金the National Natural Science Foundation of China (50772030, 50572024)
文摘BaCe0.45Zr0.45M0.1O3-δ （M=Y, In） and BaCe0.9Y0.1O3-δ were prepared through the conventional solid state reaction route. The chemical stability was investigated in hydrogen, carbon dioxide, and boiling water. Crystalline phase and microsa-ucture of the proton conductor before and after stability test were measured with X-ray diffraction （XRD） and scanning electron microscopy （SEM）, respectively. The results showed that all materials were quite stable in H2 atmosphere. In CO2 atmosphere, BaCe0.45Zr0.45M0.1O3-δ（M=Y, In） were relatively stable, while Bafe0.9Y0.1O3-δ decomposed. In boiling water, BaCe0.9Y0.1O3-δ was quickly decomposed into Ba（OH）2 and corresponding oxide. BaCe0.45Zr0.45M0.1O3-δ slightly reacted with boiling water and some amorphous phases were formed. However, BaCe0.45Zr0.45In0.1O3-δ was observed to exhibit better stability than BaCe0.45Zr0.45Y0.1O3-δ in water. The experimental results were interpreted in terms of thermodynamic data and tolerance factor.
文摘The support of catalyst for the direct synthesis of diphenyl carbonate （DPC） by heterogeneous catalytic reaction was prepared by the sol-gel method. Compared with activated charcoal, molecular sieve, porous ceramics, hopcalite, the support prepared by the sol-gel method has higher activity. The characterization of the support by X-ray diffraction （XRD） and transmission electron microscope （TEM） show that the mare crystal phase is Co2MnO4 and the average particle diameter is about 40 nm. The optimum conditions for synthesis of the support were determined by orthogonal experiments, which indicate that the proportion of Cu, Mn, and Co is the first important factor influencing the yield and selectivity of DPC. Temperature of calcination is the second one. The optimum conditions are： molar proportion of Cu, Mn, and Co being 1 ： 1 ： 1, temperature of calcination 700℃, drying at 100~C, temperature of water bath 85~C. The yield and selectivity of DPC in the process can reach 38% and 99% in the batch operation, respectively. The copper cobalt manganese mixed oxides chosen as the support contribute more to the high catalytic activity than the sol-gel method.