Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased w...Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased with the increase of Eu2O3 content in Y2O2S： Eu^3＋ （0.01 ≤ x ≤0.10）. On the other hand, the change of unit cell parameter a is not linear dependence. In the Y2O2S： Eu^3 ＋ crystal structure, Eu^3＋ ions only replaced Y^3 ＋ ions＇ places in which it posited center position of c axis. With the increase of Eu2O3 content, the position of the strongest emission peak changed from 540 nm （5D1→^ 7F2 transition） to 626 nm （^5Do→^7TF2 transition）, and the maximum intensity was obtained when x = 0.09 in Y2O2S： Eu^3＋ （0.01 ≤x ≤0.10）. This is due to the environment of trivalent europium in the crystal structure of Y2O2S. Doping with Mg^2＋ or Ti^4＋. ions alone cannot get the good long-lasting afterglow effect, whereas co-doping with Mg^2 ＋ and Ti^4 ＋ ions and excited with 365 nm ultraviolet light, a strong thermoluminesence peak appeared, red and orange long-lasting phosphorescence （LLP） was also observed and the phosphorescence lasted nearly 3 h in the light perception of the dark-adapted human eye （0.32 mcd·m^-2）. Thus the LLP mechanism was analyzed.展开更多
A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
文摘Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased with the increase of Eu2O3 content in Y2O2S： Eu^3＋ （0.01 ≤ x ≤0.10）. On the other hand, the change of unit cell parameter a is not linear dependence. In the Y2O2S： Eu^3 ＋ crystal structure, Eu^3＋ ions only replaced Y^3 ＋ ions＇ places in which it posited center position of c axis. With the increase of Eu2O3 content, the position of the strongest emission peak changed from 540 nm （5D1→^ 7F2 transition） to 626 nm （^5Do→^7TF2 transition）, and the maximum intensity was obtained when x = 0.09 in Y2O2S： Eu^3＋ （0.01 ≤x ≤0.10）. This is due to the environment of trivalent europium in the crystal structure of Y2O2S. Doping with Mg^2＋ or Ti^4＋. ions alone cannot get the good long-lasting afterglow effect, whereas co-doping with Mg^2 ＋ and Ti^4 ＋ ions and excited with 365 nm ultraviolet light, a strong thermoluminesence peak appeared, red and orange long-lasting phosphorescence （LLP） was also observed and the phosphorescence lasted nearly 3 h in the light perception of the dark-adapted human eye （0.32 mcd·m^-2）. Thus the LLP mechanism was analyzed.
基金Projects (51101096, 51002093) supported by the National Natural Science Foundation of ChinaProject (1052nm05000) supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject (J51042) supported by Leading Academic Discipline Project of the Shanghai Education Commission, China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.