A low-molecular-weight polylactide-poly(butylene succinate)(PLA-PBS)copolymer was synthesized and incorporated into polylactide(PLA)as a novel toughening agent by solvent casting.The copolymer had the same chemical ...A low-molecular-weight polylactide-poly(butylene succinate)(PLA-PBS)copolymer was synthesized and incorporated into polylactide(PLA)as a novel toughening agent by solvent casting.The copolymer had the same chemical structure and function as PLA and it was used as a plasticizer to PLA.The copolymer was blended with PLA at a weight ratio from 2 to 10 wt%.Phase separation between PLA and PLA-PBS was not observed from their scanning electron microscopy(SEM)images and the crystal structure of PLA almost remained unchanged based on the X-ray diffraction(XRD)measurement.The melt flow index(MFI)of the blends was higher as the amount of PLA-PBS increased,indicating that the block copolymer did improve the mobility of the PLA chains.Moreover,tensile tests revealed that PLA with greater PLA-PBS copolymer exhibited higher elongation at break and it reached the maximum at 8 wt%of PLA-PBS in PLA,which was around 6 times higher than that of pure PLA.Furthermore,the glass transition temperature,measured by differential scanning calorimetry(DSC),markedly decreased with an increasing amount of the copolymer as it decreased from 61.2℃ for pure PLA to 41.3℃when it was blended with 10 wt%PLA-PBS copolymer.Therefore,the PLA-PBS copolymer was shown to be a promising plasticizer for fully biobased and toughened PLA.展开更多
The molecular transfer printing（MTP） technique has been invented to fabricate chemical patterns with high fidelity using homopolymer inks. In this work, we systematically studied the effects of the molecular weights...The molecular transfer printing（MTP） technique has been invented to fabricate chemical patterns with high fidelity using homopolymer inks. In this work, we systematically studied the effects of the molecular weights of homopolymer inks and transfer conditions on the MTP process. We explored a large range of molecular weights（~3.5-56 kg·mol^（-1）） of hydroxyl-terminated polystyrene（PS-OH） and hydroxyl-terminated poly（methyl methacrylate）（PMMA-OH） in the MTP process, and found that the resulting chemical patterns on replicas from all five blends were functional and able to direct the assembly of films of the same blends. The transfer temperature and the film annealing sequences had an impact on the MTP process. MTP was sensitive to the transfer temperature and could only be performed within a certain temperature range, i.e. higher than the glass transition temperature（T_g） of copolymers and lower than the rearrangement temperature of the assembled domains. Pre-organization of the blend films was also necessary for MTP since the preferential wetting of PMMA domains at the replica surface might result in the formation of a PMMA wetting layer to prevent the presentation of underlying chemical patterns to the replica surface.展开更多
文摘A low-molecular-weight polylactide-poly(butylene succinate)(PLA-PBS)copolymer was synthesized and incorporated into polylactide(PLA)as a novel toughening agent by solvent casting.The copolymer had the same chemical structure and function as PLA and it was used as a plasticizer to PLA.The copolymer was blended with PLA at a weight ratio from 2 to 10 wt%.Phase separation between PLA and PLA-PBS was not observed from their scanning electron microscopy(SEM)images and the crystal structure of PLA almost remained unchanged based on the X-ray diffraction(XRD)measurement.The melt flow index(MFI)of the blends was higher as the amount of PLA-PBS increased,indicating that the block copolymer did improve the mobility of the PLA chains.Moreover,tensile tests revealed that PLA with greater PLA-PBS copolymer exhibited higher elongation at break and it reached the maximum at 8 wt%of PLA-PBS in PLA,which was around 6 times higher than that of pure PLA.Furthermore,the glass transition temperature,measured by differential scanning calorimetry(DSC),markedly decreased with an increasing amount of the copolymer as it decreased from 61.2℃ for pure PLA to 41.3℃when it was blended with 10 wt%PLA-PBS copolymer.Therefore,the PLA-PBS copolymer was shown to be a promising plasticizer for fully biobased and toughened PLA.
基金finically supported by the National Natural Science Foundation of China(Nos.51773201 and 51373166)“The Hundred Talents Program”from the Chinese Academy of Sciences,and Department of Science and Technology of Jilin Province(Nos.20150204027GX and 20160414032GH)
文摘The molecular transfer printing（MTP） technique has been invented to fabricate chemical patterns with high fidelity using homopolymer inks. In this work, we systematically studied the effects of the molecular weights of homopolymer inks and transfer conditions on the MTP process. We explored a large range of molecular weights（~3.5-56 kg·mol^（-1）） of hydroxyl-terminated polystyrene（PS-OH） and hydroxyl-terminated poly（methyl methacrylate）（PMMA-OH） in the MTP process, and found that the resulting chemical patterns on replicas from all five blends were functional and able to direct the assembly of films of the same blends. The transfer temperature and the film annealing sequences had an impact on the MTP process. MTP was sensitive to the transfer temperature and could only be performed within a certain temperature range, i.e. higher than the glass transition temperature（T_g） of copolymers and lower than the rearrangement temperature of the assembled domains. Pre-organization of the blend films was also necessary for MTP since the preferential wetting of PMMA domains at the replica surface might result in the formation of a PMMA wetting layer to prevent the presentation of underlying chemical patterns to the replica surface.