To prepare potassium titanate catalyst, a novel citrate acid complex-combustion method using CH3COOK and Ti（OC4H9）4 as raw materials was developed. The crystalline phase and surface morphology of K2Ti205 were invest...To prepare potassium titanate catalyst, a novel citrate acid complex-combustion method using CH3COOK and Ti（OC4H9）4 as raw materials was developed. The crystalline phase and surface morphology of K2Ti205 were investigated by X-ray diffraction （XRD）, field emission scanning electron microscope （FE-SEM） and transmission electron microscope （TEM）. The impact of some factors, such as the type of contact between K2Ti205 and soot, the content of water vapor and SO2 in exhaust, and the repeated use on catalytic activity of K2Ti205 were studied by temperature programmed reaction （TPR）. A comparison between the new method and the reported ones on catalytic activity of potassium titanate was investigated. The results showed that K2Ti205 had high catalytic activity and good stability.展开更多
Single-walled carbon nanotubes （SWNTs） possess high conductivity, mechanical strength, transparency, and flexibility, and are thus suitable for use in flexible electronics, transparent electrodes, and energy-storage...Single-walled carbon nanotubes （SWNTs） possess high conductivity, mechanical strength, transparency, and flexibility, and are thus suitable for use in flexible electronics, transparent electrodes, and energy-storage and energy-harvesting applications. However, to exploit these properties, SWNTs must be de-bundled in a surfactant solution to permit processing and use. We report a new method to prepare a SWNT-based transparent conducting film （TCF） using the diazo dye 3,3＇-（[1,1＇-biphenyl]-4,4＇-diyl）bis（4-amino naphthalene-1-sulfonic acid）, commonly known as Congo red （CR）, as a dispersant. Uniform 20-nm-thick TCFs were prepared on rigid glass and flexible polyethylene terephthalate （PET） substrates. The CR-SWNT dispersion and the CR-SWNT TCFs were characterized via UV-Vis-NIR, Raman spectroscopy, FT-IR spectroscopy, transmission electron microscopy （TEM）, field-emission scanning electron microscopy （FE-SEM） and dynamic light scattering （DLS） measurements. The sheet resistivity of the CRSWNT TCF was -34 ±6.6 Ω/□ with a transmittance of 81% at 550 nm, comparable to that of indium tin oxide-based films. Unlike SWNT dispersions prepared in common surfactants, such as sodium dodecyl sulfate （SDS）, sodium cholate （SC）, and Triton X-100, the CR-SWNT dispersion was amenable to forming TCF by drop coating. The CR-SWNT TCF was also very stable, maintaining a very low sheet resistivity even after 1,000 consecutive bending cycles of 8 mm bending radius. Further, manganese dioxide （MnO2） was electrochemically deposited on the CR-SWNT-PET film （MnO2-CR-SWNT-PET）. The as-prepared MnO2- CR-SWNT-PET electrode exhibited high specific capacitance and bendability, demonstrating promise as a candidate electrode material for flexible supercapacitors.展开更多
A series of cholesterol-appended quinacridone (QA) derivatives 1a-1d have been synthesized,in which 1b and 1c could form stable organogels in a wide range of organic solvents upon ultrasound irradiation.Field emission...A series of cholesterol-appended quinacridone (QA) derivatives 1a-1d have been synthesized,in which 1b and 1c could form stable organogels in a wide range of organic solvents upon ultrasound irradiation.Field emission scanning electronic microscope (FESEM) and transmission electron microscopy (TEM) of xerogels or precipitates indicated that 1b and 1c formed 1D fibrous nanostructure,while 1a assembled into 3D flower-like microstructures.The ultrasound-induced organogel process was characterized by kinetic UV-vis and photoluminescence spectroscopic methods suggesting the formation of ?-? aggregates in the gel state.Experimental results demonstrated that the ultrasound could promote molecules to contact frequently in the solution and induce semistable initial aggregates,which propagate to form nano/micro superstructures.The aggregation model was optimized by semiempirical AM1 calculation suggesting the hierarchical self-assembly process.In addition,the formed xerogel film exhibited mechanochromic property,and the phase transition process was accompanied by the fluorescence changes between yellowish green and orange.展开更多
基金the financial supports provided for this research by the Education Department of Liaoning Province of China(No.2009T061)the Ministry of Education of China(No.[2010]1561)
文摘To prepare potassium titanate catalyst, a novel citrate acid complex-combustion method using CH3COOK and Ti（OC4H9）4 as raw materials was developed. The crystalline phase and surface morphology of K2Ti205 were investigated by X-ray diffraction （XRD）, field emission scanning electron microscope （FE-SEM） and transmission electron microscope （TEM）. The impact of some factors, such as the type of contact between K2Ti205 and soot, the content of water vapor and SO2 in exhaust, and the repeated use on catalytic activity of K2Ti205 were studied by temperature programmed reaction （TPR）. A comparison between the new method and the reported ones on catalytic activity of potassium titanate was investigated. The results showed that K2Ti205 had high catalytic activity and good stability.
文摘Single-walled carbon nanotubes （SWNTs） possess high conductivity, mechanical strength, transparency, and flexibility, and are thus suitable for use in flexible electronics, transparent electrodes, and energy-storage and energy-harvesting applications. However, to exploit these properties, SWNTs must be de-bundled in a surfactant solution to permit processing and use. We report a new method to prepare a SWNT-based transparent conducting film （TCF） using the diazo dye 3,3＇-（[1,1＇-biphenyl]-4,4＇-diyl）bis（4-amino naphthalene-1-sulfonic acid）, commonly known as Congo red （CR）, as a dispersant. Uniform 20-nm-thick TCFs were prepared on rigid glass and flexible polyethylene terephthalate （PET） substrates. The CR-SWNT dispersion and the CR-SWNT TCFs were characterized via UV-Vis-NIR, Raman spectroscopy, FT-IR spectroscopy, transmission electron microscopy （TEM）, field-emission scanning electron microscopy （FE-SEM） and dynamic light scattering （DLS） measurements. The sheet resistivity of the CRSWNT TCF was -34 ±6.6 Ω/□ with a transmittance of 81% at 550 nm, comparable to that of indium tin oxide-based films. Unlike SWNT dispersions prepared in common surfactants, such as sodium dodecyl sulfate （SDS）, sodium cholate （SC）, and Triton X-100, the CR-SWNT dispersion was amenable to forming TCF by drop coating. The CR-SWNT TCF was also very stable, maintaining a very low sheet resistivity even after 1,000 consecutive bending cycles of 8 mm bending radius. Further, manganese dioxide （MnO2） was electrochemically deposited on the CR-SWNT-PET film （MnO2-CR-SWNT-PET）. The as-prepared MnO2- CR-SWNT-PET electrode exhibited high specific capacitance and bendability, demonstrating promise as a candidate electrode material for flexible supercapacitors.
基金supported by the National Natural Science Foundation of China (50773027 and 50733002)the National Basic Research Development Program (2009CB939700)111 Project (B06009)
文摘A series of cholesterol-appended quinacridone (QA) derivatives 1a-1d have been synthesized,in which 1b and 1c could form stable organogels in a wide range of organic solvents upon ultrasound irradiation.Field emission scanning electronic microscope (FESEM) and transmission electron microscopy (TEM) of xerogels or precipitates indicated that 1b and 1c formed 1D fibrous nanostructure,while 1a assembled into 3D flower-like microstructures.The ultrasound-induced organogel process was characterized by kinetic UV-vis and photoluminescence spectroscopic methods suggesting the formation of ?-? aggregates in the gel state.Experimental results demonstrated that the ultrasound could promote molecules to contact frequently in the solution and induce semistable initial aggregates,which propagate to form nano/micro superstructures.The aggregation model was optimized by semiempirical AM1 calculation suggesting the hierarchical self-assembly process.In addition,the formed xerogel film exhibited mechanochromic property,and the phase transition process was accompanied by the fluorescence changes between yellowish green and orange.