A sloping semisolid rheo-rolling process of Mg-3Sn-1Mn alloy was developed, and the effects of process parameters on the microstructure and mechanical properties of Mg-3Sn-lMn alloy strip were studied. The results sho...A sloping semisolid rheo-rolling process of Mg-3Sn-1Mn alloy was developed, and the effects of process parameters on the microstructure and mechanical properties of Mg-3Sn-lMn alloy strip were studied. The results show that the primary grain average diameter of the strip increases with the increase of the roll speed. The primary grain average diameter decreases firstly and then increases with the increase of the vibration frequency, and the tensile strength and elongation of the strip increase firstly and then decrease with the increase of the vibration frequency. The primary grain average diameter increases with the increase of casting temperature, and the tensile strength and elongation of the strip decrease correspondingly. When the casting temperature is 670℃, the roll speed is 52 mm/s, and the vibration frequency is 60 Hz, Mg-3Sn-1Mn alloy strip with good properties is produced. The mechanical properties of the present product are higher than those of Mg-3Sn-lMn alloy casting with the addition of 0.87% Ce （mass fraction）.展开更多
The extrusion preform of the spray-formed5A12Al alloy was hot rolled using high reduction rolling technology.By means of transmission electron microscopy(TEM),electron backscatter diffraction(EBSD)and energy dispersiv...The extrusion preform of the spray-formed5A12Al alloy was hot rolled using high reduction rolling technology.By means of transmission electron microscopy(TEM),electron backscatter diffraction(EBSD)and energy dispersive spectroscopy(EDS),the microstructure evolution was studied and the strengthening and toughening mechanism was thereby proposed.The results indicate that discontinuous and continuous dynamic recrystallization occurred during the hot rolling deformation of the spray-formed5A12Al alloy.The grain size was significantly refined and the micro-scale grains formed.Partial dynamic recrystallization leads to a significant increase of dislocation density and cellular structure.The Mg atoms were distributed in the Al matrix mainly in the presence of solid solution rather than the formation of precipitate.High solid solution of Mg atoms not only hindered the dislocation motion and increased the density of dislocation,but also exhibited a remarkable solid solution strengthening effect,which contributes to the high strength and high toughness of the as-rolled sheets.The tensile strength and elongation of spray formed5A12Al alloy at room temperature after3passes hot rolling were622MPa and20%,respectively.展开更多
基金Project(51222405) supported by the National Science Foundation of Outstanding Young Scholars of ChinaProject(51034002) supported by the National Natural Science Foundation of China+1 种基金Project(132002) supported by the Fok Ying Tong Education FoundationProject (2011CB610405) supported by the National Basic Research Program of China
文摘A sloping semisolid rheo-rolling process of Mg-3Sn-1Mn alloy was developed, and the effects of process parameters on the microstructure and mechanical properties of Mg-3Sn-lMn alloy strip were studied. The results show that the primary grain average diameter of the strip increases with the increase of the roll speed. The primary grain average diameter decreases firstly and then increases with the increase of the vibration frequency, and the tensile strength and elongation of the strip increase firstly and then decrease with the increase of the vibration frequency. The primary grain average diameter increases with the increase of casting temperature, and the tensile strength and elongation of the strip decrease correspondingly. When the casting temperature is 670℃, the roll speed is 52 mm/s, and the vibration frequency is 60 Hz, Mg-3Sn-1Mn alloy strip with good properties is produced. The mechanical properties of the present product are higher than those of Mg-3Sn-lMn alloy casting with the addition of 0.87% Ce （mass fraction）.
基金Project(2017JJ2073) supported by the Natural Science Foundation of Hunan Province,ChinaProject(15B063) supported by the Youth Research Foundation of Education Bureau of Hunan Province,China
文摘The extrusion preform of the spray-formed5A12Al alloy was hot rolled using high reduction rolling technology.By means of transmission electron microscopy(TEM),electron backscatter diffraction(EBSD)and energy dispersive spectroscopy(EDS),the microstructure evolution was studied and the strengthening and toughening mechanism was thereby proposed.The results indicate that discontinuous and continuous dynamic recrystallization occurred during the hot rolling deformation of the spray-formed5A12Al alloy.The grain size was significantly refined and the micro-scale grains formed.Partial dynamic recrystallization leads to a significant increase of dislocation density and cellular structure.The Mg atoms were distributed in the Al matrix mainly in the presence of solid solution rather than the formation of precipitate.High solid solution of Mg atoms not only hindered the dislocation motion and increased the density of dislocation,but also exhibited a remarkable solid solution strengthening effect,which contributes to the high strength and high toughness of the as-rolled sheets.The tensile strength and elongation of spray formed5A12Al alloy at room temperature after3passes hot rolling were622MPa and20%,respectively.