In order to investigate the tensile bond anchorage properties of Australian 500N steel bars in concrete, 111 pullout tests were conducted. The precise bond slip values have been gained by using the laser displacement ...In order to investigate the tensile bond anchorage properties of Australian 500N steel bars in concrete, 111 pullout tests were conducted. The precise bond slip values have been gained by using the laser displacement sensor with high resolution, including the complete bond-slip curves. How the main anchorage factors such as concrete strength, bar diameter （8, I0, 12, 16, 20, 24, 28, 32 and 36 mm） the concrete covered, embedded length and transverse reinforcement influencing the bond anchorage properties was studied under tensile condition. The process of the tensile force-slip failure for Australian 500N reinforcing steel can be divided into five stages： elastic stage, local slip stage, slip in ascent stage, slip in descent stage and remnant stage. The formula for calculating the tensile bond strength of Australian 500N reinforcing bar in concrete was proposed according to the test results, including the consistent model for tensile bond-slip relationship.展开更多
The fracture behavior of a permanent mould casting Mg-8.57Gd-3.72Y-0.54Zr(mass fraction,%)(GW94) alloy was investigated under different thermal conditions,including as-cast,solution-treated,peak-aged,and over-aged sta...The fracture behavior of a permanent mould casting Mg-8.57Gd-3.72Y-0.54Zr(mass fraction,%)(GW94) alloy was investigated under different thermal conditions,including as-cast,solution-treated,peak-aged,and over-aged states.Scanning electron microscopy(SEM) and optical microscopy(OM) were employed to examine the crack nucleation and fracture model.The results indicate that the GW94 alloy shows different behaviors of crack initiation and fracture under different thermal conditions. During tensile test at room temperature,the fracture model of the as-cast GW94 alloy is quasi-cleavage,while that of the solution-treated alloy is transgranular cleavage.It is a mixed pattern of transgranular and intergranular fracture for both the aged conditions.Large cavities formed at grain boundaries are observed in the peak-aged sample tested at 300℃,corresponding to the intergranular fracture.Localized plastic deformation at grain boundaries is also observed and corresponds to the high elongation at 300℃.展开更多
The effects of coagulation conditions on tensile properties of the regenerated cellulose fibers prepared by wet-spinning from NaOH/thiourea/urea(8∶6.5∶8 by weight)aqueous solvent were investigated by tensile tester,...The effects of coagulation conditions on tensile properties of the regenerated cellulose fibers prepared by wet-spinning from NaOH/thiourea/urea(8∶6.5∶8 by weight)aqueous solvent were investigated by tensile tester,X-ray diffraction(XRD),and scanning electron microscope(SEM).The results show that the tensile properties of the as-spun fibers change with the coagualtion concentration,temperature,and time.When the spinning solution is coagulated in 10% H2SO4/12.5% Na2SO4 aqueous solution,the as-spun fibers have a typical structure of cellulose II,a circular cross-section,and homogeneous morphological structure.展开更多
Stress intensity factors of thin AZ31B magnesium alloy sheet under biaxial tension loading were analyzed by modified Dugdale model. K-values with crack angle of 90° obviously show that there is no influence of th...Stress intensity factors of thin AZ31B magnesium alloy sheet under biaxial tension loading were analyzed by modified Dugdale model. K-values with crack angle of 90° obviously show that there is no influence of the loading condition in Mode-I. In the 45° case, K1 values are obtained within 10% errors when they are calculated by modified Dugdale model under biaxial loading. It is concluded that the modified Dugdale model is one of effective ways to evaluate stress intensity factor of AZ31 magnesium alloy sheet appropriately.展开更多
基金Project(DP0988940) supported by Australian Research Council Discovery Grant Program Project(2011M500930) supported by Postdoctoral Science Foundation of China+1 种基金Project(11KJB560003) supported by College Natural Science Foundation of Jiangsu Province,ChinaProject(163050072) supported by the Talent Introduction Foundation of Nanjing Forestry University,China
文摘In order to investigate the tensile bond anchorage properties of Australian 500N steel bars in concrete, 111 pullout tests were conducted. The precise bond slip values have been gained by using the laser displacement sensor with high resolution, including the complete bond-slip curves. How the main anchorage factors such as concrete strength, bar diameter （8, I0, 12, 16, 20, 24, 28, 32 and 36 mm） the concrete covered, embedded length and transverse reinforcement influencing the bond anchorage properties was studied under tensile condition. The process of the tensile force-slip failure for Australian 500N reinforcing steel can be divided into five stages： elastic stage, local slip stage, slip in ascent stage, slip in descent stage and remnant stage. The formula for calculating the tensile bond strength of Australian 500N reinforcing bar in concrete was proposed according to the test results, including the consistent model for tensile bond-slip relationship.
基金Project(2007CB613704) supported by the National Basic Research Program of China
文摘The fracture behavior of a permanent mould casting Mg-8.57Gd-3.72Y-0.54Zr(mass fraction,%)(GW94) alloy was investigated under different thermal conditions,including as-cast,solution-treated,peak-aged,and over-aged states.Scanning electron microscopy(SEM) and optical microscopy(OM) were employed to examine the crack nucleation and fracture model.The results indicate that the GW94 alloy shows different behaviors of crack initiation and fracture under different thermal conditions. During tensile test at room temperature,the fracture model of the as-cast GW94 alloy is quasi-cleavage,while that of the solution-treated alloy is transgranular cleavage.It is a mixed pattern of transgranular and intergranular fracture for both the aged conditions.Large cavities formed at grain boundaries are observed in the peak-aged sample tested at 300℃,corresponding to the intergranular fracture.Localized plastic deformation at grain boundaries is also observed and corresponds to the high elongation at 300℃.
文摘The effects of coagulation conditions on tensile properties of the regenerated cellulose fibers prepared by wet-spinning from NaOH/thiourea/urea(8∶6.5∶8 by weight)aqueous solvent were investigated by tensile tester,X-ray diffraction(XRD),and scanning electron microscope(SEM).The results show that the tensile properties of the as-spun fibers change with the coagualtion concentration,temperature,and time.When the spinning solution is coagulated in 10% H2SO4/12.5% Na2SO4 aqueous solution,the as-spun fibers have a typical structure of cellulose II,a circular cross-section,and homogeneous morphological structure.
文摘Stress intensity factors of thin AZ31B magnesium alloy sheet under biaxial tension loading were analyzed by modified Dugdale model. K-values with crack angle of 90° obviously show that there is no influence of the loading condition in Mode-I. In the 45° case, K1 values are obtained within 10% errors when they are calculated by modified Dugdale model under biaxial loading. It is concluded that the modified Dugdale model is one of effective ways to evaluate stress intensity factor of AZ31 magnesium alloy sheet appropriately.