The heterogeneity ofα-Al(Fe,Mn)Si dispersoids andβ″precipitates was tuned to enhance the strength−ductility synergy of air-cooled Al−Mg−Si alloys.Scanning electron microscopy(SEM)and transmission electron microscop...The heterogeneity ofα-Al(Fe,Mn)Si dispersoids andβ″precipitates was tuned to enhance the strength−ductility synergy of air-cooled Al−Mg−Si alloys.Scanning electron microscopy(SEM)and transmission electron microscopy(TEM)were employed to elucidate the microstructural parameters of these two strengthening phases.The results show that the microstructural heterogeneity can be triggered by the absence of homogenization,resulting in the presence of dispersoid-free zones(DFZs)and dispersoid zones(DZs),in conjunction with bimodalβ″precipitates.Further analytical calculations,from the strengthening model,clarify that the strategically dispersedα-Al(Fe,Mn)Si andβ″particles create“soft”and“hard”domains within the alloy,resultantly improving the mechanical properties.展开更多
The microstructure and mechanical properties of dissimilar pinless friction stir spot welded joint of2A12aluminum alloy and TC4titanium alloy were evaluated.The results show that the joint of Al/Ti dissimilar alloys c...The microstructure and mechanical properties of dissimilar pinless friction stir spot welded joint of2A12aluminum alloy and TC4titanium alloy were evaluated.The results show that the joint of Al/Ti dissimilar alloys can be successfully attained through pinless friction stir spot welding(FSSW).The joint can be divided into three zones(SZ,TMAZ and HAZ).The microstructure of joint in Al alloy side changes significantly but it basically has no change in Ti alloy side.At the same rotation speed,the maximum load of welded joints gradually rises with the increase in dwell time.At the same dwell time,the maximum load of the welded joint increases with the increase of the rotational speed.In addition,optimal parameters were obtained in this work,and they are rotation speed of1500r/min,plunge speed of30mm/min,plunge depth of0.3mm and dwell time of15s.The fracture mode of welded joints is interfacial shear fracture.The microhardness of the joint on the Al side distributes in a typical“W”type and is symmetry along the weld center,but the distribution of the microhardness on the Ti side has no obvious change.展开更多
基金supported by the National Natural Science Foundation of China(Nos.52301025,52371065,52301179)the Fundamental Research Program of Shanxi Province,China(Nos.202203021222039,202203021212124)。
文摘The heterogeneity ofα-Al(Fe,Mn)Si dispersoids andβ″precipitates was tuned to enhance the strength−ductility synergy of air-cooled Al−Mg−Si alloys.Scanning electron microscopy(SEM)and transmission electron microscopy(TEM)were employed to elucidate the microstructural parameters of these two strengthening phases.The results show that the microstructural heterogeneity can be triggered by the absence of homogenization,resulting in the presence of dispersoid-free zones(DFZs)and dispersoid zones(DZs),in conjunction with bimodalβ″precipitates.Further analytical calculations,from the strengthening model,clarify that the strategically dispersedα-Al(Fe,Mn)Si andβ″particles create“soft”and“hard”domains within the alloy,resultantly improving the mechanical properties.
基金Projects(51405389,51675435)supported by the National Natural Science Foundation of ChinaProject(3102017ZY005)supported by the Fundamental Research Funds for the Central Universities,China+3 种基金Project(SAST2016043)supported by the Fund of SAST,ChinaProject(20161125002)supported by the Aeronautical Science Foundation of ChinaProject(B08040)supported by the 111 Project,ChinaProjects(2016YFB0701203,2016YFB1100104)supported by the National Key Research and Development Program of China
文摘The microstructure and mechanical properties of dissimilar pinless friction stir spot welded joint of2A12aluminum alloy and TC4titanium alloy were evaluated.The results show that the joint of Al/Ti dissimilar alloys can be successfully attained through pinless friction stir spot welding(FSSW).The joint can be divided into three zones(SZ,TMAZ and HAZ).The microstructure of joint in Al alloy side changes significantly but it basically has no change in Ti alloy side.At the same rotation speed,the maximum load of welded joints gradually rises with the increase in dwell time.At the same dwell time,the maximum load of the welded joint increases with the increase of the rotational speed.In addition,optimal parameters were obtained in this work,and they are rotation speed of1500r/min,plunge speed of30mm/min,plunge depth of0.3mm and dwell time of15s.The fracture mode of welded joints is interfacial shear fracture.The microhardness of the joint on the Al side distributes in a typical“W”type and is symmetry along the weld center,but the distribution of the microhardness on the Ti side has no obvious change.