The lithology of fracture zone which was developed at the dam foundation of a hydropower station is weak sandstone with poor integrity and pore cementation contact.Its creep properties have a significant impact on the...The lithology of fracture zone which was developed at the dam foundation of a hydropower station is weak sandstone with poor integrity and pore cementation contact.Its creep properties have a significant impact on the deformation and stability of the dam.Based on the characteristics of loose organizational structure,high moisture content and poor mechanical properties,the triaxial compression tests and creep tests were carried out,respectively.The results show significant non-linear,low strength and no obvious strength peaks.Both axial and lateral strains are achieved more than 3%when the tests are failed.The weak sandstone has a significant creep property,but only transient and steady state appear under low stress.Increased stress causes creep intensified and lateral strain gradually exceeds axial strain.In the failure stage,it has characteristics of large axial plastic deformation,obvious volumetric ductility dilation and large steady creep rate.The accelerated creep appears shortly after transient loading under confining of pressures 1.0 MPa and 1.5 MPa.Therefore,an improved Burgers creep model considering the non-linear characteristics of weak sandstone is built based on hyperbolic equation and the creep parameters are identified.This model can well describe the creep properties of weak sandstone.展开更多
Tensile creep behaviors of the ageing hardened Mg-10Gd-3Y alloy(referred to GW103)were investigated at temperatures up to 300℃.The extruded-T5 specimen exhibited high creep resistance,i.e.the low steady-state creep r...Tensile creep behaviors of the ageing hardened Mg-10Gd-3Y alloy(referred to GW103)were investigated at temperatures up to 300℃.The extruded-T5 specimen exhibited high creep resistance,i.e.the low steady-state creep rate and long creep rupture time,while the better creep properties were observed in the cast-T6 one.The low steady-state creep rate of 1.71×10- 9s -1is obtained at 200℃and 80 MPa for the extruded-T5 GW103 alloy.In addition,the microstructure development of GW103-T5 alloy was also examined after creep exposure at different temperatures.On the other hand,the stress exponent and activation energy were studied in the temperature range of 200-300℃for the extruded-T5 specimens,and the creep mechanism was also discussed.展开更多
基金Project(2011CB013504)supported by the National Basic Research Program of ChinaProject(11172090)supported by the National Natural Science Foundation of China
文摘The lithology of fracture zone which was developed at the dam foundation of a hydropower station is weak sandstone with poor integrity and pore cementation contact.Its creep properties have a significant impact on the deformation and stability of the dam.Based on the characteristics of loose organizational structure,high moisture content and poor mechanical properties,the triaxial compression tests and creep tests were carried out,respectively.The results show significant non-linear,low strength and no obvious strength peaks.Both axial and lateral strains are achieved more than 3%when the tests are failed.The weak sandstone has a significant creep property,but only transient and steady state appear under low stress.Increased stress causes creep intensified and lateral strain gradually exceeds axial strain.In the failure stage,it has characteristics of large axial plastic deformation,obvious volumetric ductility dilation and large steady creep rate.The accelerated creep appears shortly after transient loading under confining of pressures 1.0 MPa and 1.5 MPa.Therefore,an improved Burgers creep model considering the non-linear characteristics of weak sandstone is built based on hyperbolic equation and the creep parameters are identified.This model can well describe the creep properties of weak sandstone.
基金Project(2007CB613704)supported by the National Basic Research Program of ChinaProject(50874100)supported by the National Natural Science Foundation of China
文摘Tensile creep behaviors of the ageing hardened Mg-10Gd-3Y alloy(referred to GW103)were investigated at temperatures up to 300℃.The extruded-T5 specimen exhibited high creep resistance,i.e.the low steady-state creep rate and long creep rupture time,while the better creep properties were observed in the cast-T6 one.The low steady-state creep rate of 1.71×10- 9s -1is obtained at 200℃and 80 MPa for the extruded-T5 GW103 alloy.In addition,the microstructure development of GW103-T5 alloy was also examined after creep exposure at different temperatures.On the other hand,the stress exponent and activation energy were studied in the temperature range of 200-300℃for the extruded-T5 specimens,and the creep mechanism was also discussed.