The severe cold rolling was employed to enhance strength of Mg-3Gd-lZn （mass fraction, %） alloy sheet. The 0.2% yield stress of the Mg-3Gd-1Zn hot-rolled sheet can be increased by 150% through the single-pass cold r...The severe cold rolling was employed to enhance strength of Mg-3Gd-lZn （mass fraction, %） alloy sheet. The 0.2% yield stress of the Mg-3Gd-1Zn hot-rolled sheet can be increased by 150% through the single-pass cold rolling with the reduction of 23%, due to the high intensity of dislocation and basal texture established during cold rolling. Compared with the Mg-3Gd-lZn hot-rolled sheet, the cold-rolled sheet annealed at 350 for 30 min may get an enhancement in strength without a great loss of ductility. The sheet processed by multi-pass cold rolling does not show a higher strength as expected, due to the softening effect of shear bands. However, the thin slab with the thickness less than 1 mm can be produced by the multi-pass cold rolling with the annealing treatment as few as possible.展开更多
TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The ...TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The results show that the TA2 part of exhibiting near-equiaxed grains was Widmanst？tten α-laths microstructure. The TA15 part containing large columnar grains was fine basket-weave microstructure. The graded zone was divided into four deposited layers with 3000 μm in thickness. As the distance from the TA2 part increases, the alloy element contents and the β phase volume fraction increase, the α phase volume fraction decreases and the microstructure shows the evolution from Widmanst？tten α-laths to basket-weave α-laths gradually. The micro-hardness increases from the TA2 part to the TA15 part due to the solid solution strengthening and grain boundary strengthening.展开更多
Short carbon fiber felts with an initial porosity of 89.5% were deposited by isobaric, isothermal chemical vapor infiltration using natural gas as carbon source. The bulk density of the deposited carbon/carbon （C/C）...Short carbon fiber felts with an initial porosity of 89.5% were deposited by isobaric, isothermal chemical vapor infiltration using natural gas as carbon source. The bulk density of the deposited carbon/carbon （C/C） composites was 1.89 g/cm3 after depositing for 150 h. The microstructure and mechanical properties of the C/C composites were studied by polarized light microscopy, X-ray diffraction, scanning electron microscopy and three-point bending test. The results reveal that high textured pyrolytic carbon is deposited as the matrix of the composites, whose crystalline thickness and graphitization degree highly increase after heat treatment. A distinct decrease of the flexural strength and modulus accompanied by the increase of the toughness of the C/C composites is found to be correlated with the structural changes in the composites during the heat treatment process.展开更多
2195 Al-Li alloy was deformed through extrusion followed by cold-rolling.The textures of the extruded plate and cold-rolled sheet after solutionization were investigated.The longitudinal strength and precipitates afte...2195 Al-Li alloy was deformed through extrusion followed by cold-rolling.The textures of the extruded plate and cold-rolled sheet after solutionization were investigated.The longitudinal strength and precipitates after T8 aging were measured and observed,respectively.Compared to those in the sheet,T1(Al2 Cu Li)precipitates in the extruded plate after T8 aging are non-uniform,and their incubation time is shorter.The extruded plate after solutionization is not recrystallized and contains 55.28%deformation textures of Brass and S.In the cold-rolled sheet after solutionization,massive recrystallization occurs and S component disappears.Due to the higher fraction of Brass and S textures with higher Schmid factor and lower equivalent sliding system number,the extruded plate possesses an yield strength not higher or even lower,but a tensile strength higher,than the cold-rolled sheet after solutionization.In addition,during the aging after pre-stretch,these textures promote T1 precipitation on preferred sliding planes of cold-rolled sheet and cause its higher yield strength and tensile strength after T8 aging.展开更多
To clarify the influence of the deformation texture on the mechanical properties,pure Mo plates were processed by various cross rolling procedures,and the relation among texture,microstructure and mechanical propertie...To clarify the influence of the deformation texture on the mechanical properties,pure Mo plates were processed by various cross rolling procedures,and the relation among texture,microstructure and mechanical properties was discussed.The results show that cross rolling of the Mo plates is beneficial for the formation of the rotated cube component,i.e.,{001}<110>.The corresponding orientation density exhibits a positive correlation with the total rolling deformation and the current-pass deformation.When the total deformation is 96%or greater,the Mo plates form a texture orientation dominated by{001}<110>,whereas theγ-fibre texture becomes weaker and the cube texture{100}<100>disappears completely.The presence of{001}<110>has great effects on the properties of cross-rolled Mo plates,which is beneficial for strength enhancement and plasticity reduction in both the rolling direction(RD)and the transverse direction(TD).展开更多
The biocompatibility of orthopedic implants is closely related to their elastic modulus and surface properties.The objective of this study was to determine the effects of cold rolling,recrystallization and laser surfa...The biocompatibility of orthopedic implants is closely related to their elastic modulus and surface properties.The objective of this study was to determine the effects of cold rolling,recrystallization and laser surface melting(LSM)on the microstructure and mechanical properties of a biphase(α″+β)Ti-30Nb-4Sn alloy.X-ray diffraction(XRD)texture analysis of the cold-rolled substrate revealed the[302]α″//ND texture component,while analysis of the recrystallized substrate showed the[302]α″//ND and[110]α″//ND components.Theβ-phase texture could not be directly measured by XRD,but the presence of the[111]β//ND texture component was successfully predicted by considering the orientation relationship between theα″andβphases.Nanoindentation measurements showed that the elastic modulus of the cold-rolled substrate(63GPa)was lower than that of the recrystallized substrate(74GPa).Based on the available literature and the results presented here,it is suggested that this difference is caused by the introduction of crystal defects during cold deformation.The combined nanoindentation/EBSD analysis showed that the nanoindentation results are not affected by crystal orientation.LSM of the deformed alloy produced changes in hardness,elastic modulus and crystallographic texture similar to those produced by recrystallization heat treatment,creating a stiffness gradient between surface and substrate.展开更多
Asymmetric lowered-temperature rolling was applied to the fabrication of fine-grained ZK60 magnesium alloy sheet with weak basal texture along the rolling direction(RD).The results showed that multi-pass lowered-tempe...Asymmetric lowered-temperature rolling was applied to the fabrication of fine-grained ZK60 magnesium alloy sheet with weak basal texture along the rolling direction(RD).The results showed that multi-pass lowered-temperature rolling could significantly improve the microstructure homogeneity and refine the grain size.Meanwhile,a fiber texture along the transverse direction(TD)gradually developed during rolling process.Importantly,the shear deformation along the RD made the c-axis of basal plane rotate to the RD,weakening the basal texture along this direction.Influenced by such microstructure variation,the yield strength along the TD continuously increased due to the successive grain refinement and the increased activation of prismatic slips,whereas the uniform elongation decreased owing to the decline of strain hardening ability.In contrast,the continuous weakening of basal texture along the RD increased the activation of soft basal slips,greatly offsetting the strengthening effect contributed by grain refinement and thereby causing the slight decrease of yield strength.展开更多
Spherical Ni（OH）2 particles were prepared by an aqueous solution precipitation route. The structure of spherical Ni（OH）2 was investigated by scanning electron microscopy and transmission electron microscopy and co...Spherical Ni（OH）2 particles were prepared by an aqueous solution precipitation route. The structure of spherical Ni（OH）2 was investigated by scanning electron microscopy and transmission electron microscopy and compared with that of traditional Ni（OH）2. The results show that the spherical nickel hydroxide consists of （Ni（OH）2） spheres with a reticulate structure of platelet-like, which is almost arranged radially and the crystalline grains intervene and connect with each other to form a three-dimensional net. The spherical Ni（OH）2 particle is full of pores, crannies between cleave planes. It is supposed that this structure is beneficial to the structural stability for the spherical particles during the charge/discharge processes and can improve the cycle life of the electrode; the pores and the crannies in spherical particles can shorten the proton diffusion distance and speed its velocity, which may result in that the local polarization is lowered. The electrochemical performances of the spherical Ni（OH）2 are improved by enhancing the conducting properties of the crystalline lattice due to its quick proton diffusion.展开更多
In order to simultaneously improve strength and formability,an analytical model for the concentration distribution of precipitates and solute elements is established and used to theoretically design and control the he...In order to simultaneously improve strength and formability,an analytical model for the concentration distribution of precipitates and solute elements is established and used to theoretically design and control the heterogeneous microstructure of Al−Zn−Mg−Cu alloys.The results show that the dissolution of precipitates is mainly affected by particle size and heat treatment temperature,the heterogeneous distribution level of solute elements diffused in the alloy matrix mainly depends on the grain size,while the heat treatment temperature only has an obvious effect on the concentration distribution in the larger grains,and the experimental results of Al−Zn−Mg−Cu alloy are in good agreement with the theoretical model predictions of precipitates and solute element concentration distribution.Controlling the concentration distribution of precipitates and solute elements in Al−Zn−Mg−Cu alloys is the premise of accurately constructing heterogeneous microstructure in micro-domains,which can be used to significantly improve the formability of Al−Zn−Mg−Cu alloys with a heterostructure.展开更多
With the experiment and finite element simulation, the influences of power ultrasonic on the solidification structure of 7050 aluminum alloy ingot in semi-continuous casting were researched, and the effects of casting...With the experiment and finite element simulation, the influences of power ultrasonic on the solidification structure of 7050 aluminum alloy ingot in semi-continuous casting were researched, and the effects of casting speed on solidification structure in ultrasonic field were also analyzed. The experiment and simulation results show that the solidification structure of the ingot is homogeneously distributed, and its grain size is obviously refined at ultrasonic power of 240 W. The average grain sizes, which can be seen from the Leica microscope, are less than 100 μm. When the casting speed is 45-50 mm/min, the best grain refinement is obtained.展开更多
By inserting the variable of the exactness of corporate valuation into the classic model of Contract Theory, this paper, on the bases of the interaction of the variables of the veraciousness of corporate valuation, ma...By inserting the variable of the exactness of corporate valuation into the classic model of Contract Theory, this paper, on the bases of the interaction of the variables of the veraciousness of corporate valuation, managerial incentives and operational risks, explores the deep-seated reasons for changes in corporate structures, and draws the conclusion that the divestment of the subsidiary is beneficial to shareholders when the parent corporate is undervalued and that the relation between the parent and the subsidiary is disordered, or vice versa. This conclusion is consistent with the motives of many divestiture cases in reality.展开更多
Non-profit organizations （NPOs） in Malaysia are not subjected to statutory requirement to follow the accounting standards when preparing their annual reports. This study analyzed the annual reports of 100 NPOs regis...Non-profit organizations （NPOs） in Malaysia are not subjected to statutory requirement to follow the accounting standards when preparing their annual reports. This study analyzed the annual reports of 100 NPOs registered with the Registry of Society （ROS） under the charity and religious categories. The objectives of this study are： （1） to determine the current state of reporting practices by NPOs; and （2） to describe the contents of a set of annual reports and the financial statement presentation of NPOs. This study found that there were variations in reporting practices among the charity and religious categories of NPOs. On average, the results show that NPOs do not focus on the disclosing information required by the ROS, the governing body of NPOs. This indicates that the regulators need to strongly practice enforcement to strengthen the compliance of the annual reports submission. Overall, the findings of this study provide useful information to regulators as a basis for preparing and presenting NPOs＇ annual report framework in the future.展开更多
基金Project (2013CB632202) supported by the National Basic Research Program of ChinaProject (51105350) supported by the National Natural Science Foundation of China
文摘The severe cold rolling was employed to enhance strength of Mg-3Gd-lZn （mass fraction, %） alloy sheet. The 0.2% yield stress of the Mg-3Gd-1Zn hot-rolled sheet can be increased by 150% through the single-pass cold rolling with the reduction of 23%, due to the high intensity of dislocation and basal texture established during cold rolling. Compared with the Mg-3Gd-lZn hot-rolled sheet, the cold-rolled sheet annealed at 350 for 30 min may get an enhancement in strength without a great loss of ductility. The sheet processed by multi-pass cold rolling does not show a higher strength as expected, due to the softening effect of shear bands. However, the thin slab with the thickness less than 1 mm can be produced by the multi-pass cold rolling with the annealing treatment as few as possible.
基金Project(2010CB731705)supported by the National Basic Research Program of China
文摘TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The results show that the TA2 part of exhibiting near-equiaxed grains was Widmanst？tten α-laths microstructure. The TA15 part containing large columnar grains was fine basket-weave microstructure. The graded zone was divided into four deposited layers with 3000 μm in thickness. As the distance from the TA2 part increases, the alloy element contents and the β phase volume fraction increase, the α phase volume fraction decreases and the microstructure shows the evolution from Widmanst？tten α-laths to basket-weave α-laths gradually. The micro-hardness increases from the TA2 part to the TA15 part due to the solid solution strengthening and grain boundary strengthening.
基金Projects(51221001,50972121)supported by the National Natural Science Foundation of ChinaProject(B08040)supported by the Introducing Talents of Discipline to Universities,ChinaProject(11-BZ-2012)supported by the Research Fund of the State Key Laboratory of Solidification Processing(NWPU),China
文摘Short carbon fiber felts with an initial porosity of 89.5% were deposited by isobaric, isothermal chemical vapor infiltration using natural gas as carbon source. The bulk density of the deposited carbon/carbon （C/C） composites was 1.89 g/cm3 after depositing for 150 h. The microstructure and mechanical properties of the C/C composites were studied by polarized light microscopy, X-ray diffraction, scanning electron microscopy and three-point bending test. The results reveal that high textured pyrolytic carbon is deposited as the matrix of the composites, whose crystalline thickness and graphitization degree highly increase after heat treatment. A distinct decrease of the flexural strength and modulus accompanied by the increase of the toughness of the C/C composites is found to be correlated with the structural changes in the composites during the heat treatment process.
基金Project(2013AA032401)supported by the National High Technology Research and Development Program of China。
文摘2195 Al-Li alloy was deformed through extrusion followed by cold-rolling.The textures of the extruded plate and cold-rolled sheet after solutionization were investigated.The longitudinal strength and precipitates after T8 aging were measured and observed,respectively.Compared to those in the sheet,T1(Al2 Cu Li)precipitates in the extruded plate after T8 aging are non-uniform,and their incubation time is shorter.The extruded plate after solutionization is not recrystallized and contains 55.28%deformation textures of Brass and S.In the cold-rolled sheet after solutionization,massive recrystallization occurs and S component disappears.Due to the higher fraction of Brass and S textures with higher Schmid factor and lower equivalent sliding system number,the extruded plate possesses an yield strength not higher or even lower,but a tensile strength higher,than the cold-rolled sheet after solutionization.In addition,during the aging after pre-stretch,these textures promote T1 precipitation on preferred sliding planes of cold-rolled sheet and cause its higher yield strength and tensile strength after T8 aging.
基金Project(2017YFB0306001)supported by the National Key R&D Program of ChinaProject(502221802)supported by the Innovation-Driven Project of Central South University,China。
文摘To clarify the influence of the deformation texture on the mechanical properties,pure Mo plates were processed by various cross rolling procedures,and the relation among texture,microstructure and mechanical properties was discussed.The results show that cross rolling of the Mo plates is beneficial for the formation of the rotated cube component,i.e.,{001}<110>.The corresponding orientation density exhibits a positive correlation with the total rolling deformation and the current-pass deformation.When the total deformation is 96%or greater,the Mo plates form a texture orientation dominated by{001}<110>,whereas theγ-fibre texture becomes weaker and the cube texture{100}<100>disappears completely.The presence of{001}<110>has great effects on the properties of cross-rolled Mo plates,which is beneficial for strength enhancement and plasticity reduction in both the rolling direction(RD)and the transverse direction(TD).
基金supported by the Brazilian Funding Agencies CAPES(Federal Agency for the Support and Improvement of Higher Education)(Grant No.33003017)CNPq(National Council for Scientific and Technological Development)(Grant No.233006/2014-1)FAPESP(Sao Paulo Research Foundation)(Grant No.2011/19982-2)
文摘The biocompatibility of orthopedic implants is closely related to their elastic modulus and surface properties.The objective of this study was to determine the effects of cold rolling,recrystallization and laser surface melting(LSM)on the microstructure and mechanical properties of a biphase(α″+β)Ti-30Nb-4Sn alloy.X-ray diffraction(XRD)texture analysis of the cold-rolled substrate revealed the[302]α″//ND texture component,while analysis of the recrystallized substrate showed the[302]α″//ND and[110]α″//ND components.Theβ-phase texture could not be directly measured by XRD,but the presence of the[111]β//ND texture component was successfully predicted by considering the orientation relationship between theα″andβphases.Nanoindentation measurements showed that the elastic modulus of the cold-rolled substrate(63GPa)was lower than that of the recrystallized substrate(74GPa).Based on the available literature and the results presented here,it is suggested that this difference is caused by the introduction of crystal defects during cold deformation.The combined nanoindentation/EBSD analysis showed that the nanoindentation results are not affected by crystal orientation.LSM of the deformed alloy produced changes in hardness,elastic modulus and crystallographic texture similar to those produced by recrystallization heat treatment,creating a stiffness gradient between surface and substrate.
基金supported by the National Natural Science Foundation of China (Nos. 51975146, 51801192, 52205344)the Natural Science Foundation of Shandong Province, China (No. ZR2020QE171)+1 种基金Key Research and Development Plan in Shandong Province, China (No. 2019JZZY010364)the National Defense Basic Scientific Research of China (No. JCK2018603C017)
文摘Asymmetric lowered-temperature rolling was applied to the fabrication of fine-grained ZK60 magnesium alloy sheet with weak basal texture along the rolling direction(RD).The results showed that multi-pass lowered-temperature rolling could significantly improve the microstructure homogeneity and refine the grain size.Meanwhile,a fiber texture along the transverse direction(TD)gradually developed during rolling process.Importantly,the shear deformation along the RD made the c-axis of basal plane rotate to the RD,weakening the basal texture along this direction.Influenced by such microstructure variation,the yield strength along the TD continuously increased due to the successive grain refinement and the increased activation of prismatic slips,whereas the uniform elongation decreased owing to the decline of strain hardening ability.In contrast,the continuous weakening of basal texture along the RD increased the activation of soft basal slips,greatly offsetting the strengthening effect contributed by grain refinement and thereby causing the slight decrease of yield strength.
基金Project(50134020) supported by the National Natural Science Foundation of China
文摘Spherical Ni（OH）2 particles were prepared by an aqueous solution precipitation route. The structure of spherical Ni（OH）2 was investigated by scanning electron microscopy and transmission electron microscopy and compared with that of traditional Ni（OH）2. The results show that the spherical nickel hydroxide consists of （Ni（OH）2） spheres with a reticulate structure of platelet-like, which is almost arranged radially and the crystalline grains intervene and connect with each other to form a three-dimensional net. The spherical Ni（OH）2 particle is full of pores, crannies between cleave planes. It is supposed that this structure is beneficial to the structural stability for the spherical particles during the charge/discharge processes and can improve the cycle life of the electrode; the pores and the crannies in spherical particles can shorten the proton diffusion distance and speed its velocity, which may result in that the local polarization is lowered. The electrochemical performances of the spherical Ni（OH）2 are improved by enhancing the conducting properties of the crystalline lattice due to its quick proton diffusion.
基金financially supported by the National Key Research and Development Program of China (No. 2021YFE0115900)the National Natural Science Foundation of China (Nos. 51871029, 51571023, 51301016)+1 种基金the Government Guided Program-Intergovernmental Bilateral Innovation Cooperation Project, China (No. BZ2019019)the Opening Project of State Key Lab of Advanced Metals and Materials, China (No. 2020-ZD02)。
文摘In order to simultaneously improve strength and formability,an analytical model for the concentration distribution of precipitates and solute elements is established and used to theoretically design and control the heterogeneous microstructure of Al−Zn−Mg−Cu alloys.The results show that the dissolution of precipitates is mainly affected by particle size and heat treatment temperature,the heterogeneous distribution level of solute elements diffused in the alloy matrix mainly depends on the grain size,while the heat treatment temperature only has an obvious effect on the concentration distribution in the larger grains,and the experimental results of Al−Zn−Mg−Cu alloy are in good agreement with the theoretical model predictions of precipitates and solute element concentration distribution.Controlling the concentration distribution of precipitates and solute elements in Al−Zn−Mg−Cu alloys is the premise of accurately constructing heterogeneous microstructure in micro-domains,which can be used to significantly improve the formability of Al−Zn−Mg−Cu alloys with a heterostructure.
基金Project(2010CB731700) supported by the National Basic Research Program of China
文摘With the experiment and finite element simulation, the influences of power ultrasonic on the solidification structure of 7050 aluminum alloy ingot in semi-continuous casting were researched, and the effects of casting speed on solidification structure in ultrasonic field were also analyzed. The experiment and simulation results show that the solidification structure of the ingot is homogeneously distributed, and its grain size is obviously refined at ultrasonic power of 240 W. The average grain sizes, which can be seen from the Leica microscope, are less than 100 μm. When the casting speed is 45-50 mm/min, the best grain refinement is obtained.
文摘By inserting the variable of the exactness of corporate valuation into the classic model of Contract Theory, this paper, on the bases of the interaction of the variables of the veraciousness of corporate valuation, managerial incentives and operational risks, explores the deep-seated reasons for changes in corporate structures, and draws the conclusion that the divestment of the subsidiary is beneficial to shareholders when the parent corporate is undervalued and that the relation between the parent and the subsidiary is disordered, or vice versa. This conclusion is consistent with the motives of many divestiture cases in reality.
文摘Non-profit organizations （NPOs） in Malaysia are not subjected to statutory requirement to follow the accounting standards when preparing their annual reports. This study analyzed the annual reports of 100 NPOs registered with the Registry of Society （ROS） under the charity and religious categories. The objectives of this study are： （1） to determine the current state of reporting practices by NPOs; and （2） to describe the contents of a set of annual reports and the financial statement presentation of NPOs. This study found that there were variations in reporting practices among the charity and religious categories of NPOs. On average, the results show that NPOs do not focus on the disclosing information required by the ROS, the governing body of NPOs. This indicates that the regulators need to strongly practice enforcement to strengthen the compliance of the annual reports submission. Overall, the findings of this study provide useful information to regulators as a basis for preparing and presenting NPOs＇ annual report framework in the future.