Abstract： In order to improve the reactivity of Na2CO3/Al2O3 sorbent with CO2, a new sorbent showing high reactivity was developed by doping Na2CO3/Al2O3 with TiO2 using impregnation. Fourteen multi-cycle carbonation...Abstract： In order to improve the reactivity of Na2CO3/Al2O3 sorbent with CO2, a new sorbent showing high reactivity was developed by doping Na2CO3/Al2O3 with TiO2 using impregnation. Fourteen multi-cycle carbonation/regeneration tests of the sorbent were carried out in a fluidized-bed reactor and the sorbent was characterized by X-ray diffraction and nitrogen adsorption. It is confirmed that TiO2 shows a positive effect on the adsorption process of Na2CO3 and the reaction rate is observed to increase significantly, especially in the first 10 min. Moreover, TiO2 is stable within the temperature range of the process and no other Ti-compounds are detected. The carbonation products are NaHCO3 and Na5H3 （CO3 ）4. The surface area and the pore volume of the sorbent keep stable after 14 cycles. The Fourier transform infrared spectroscopy and the X-ray photoelectron spectroscopy are used to analyze the effect mechanism of TiO2 on CO2 adsorption process of Na2CO3/Al2O3.展开更多
基金The National Natural Science Foundation of China(No.51476030)the Specialized Research Fund for the Doctoral Program of Higher Education(No.20130092110006)
文摘Abstract： In order to improve the reactivity of Na2CO3/Al2O3 sorbent with CO2, a new sorbent showing high reactivity was developed by doping Na2CO3/Al2O3 with TiO2 using impregnation. Fourteen multi-cycle carbonation/regeneration tests of the sorbent were carried out in a fluidized-bed reactor and the sorbent was characterized by X-ray diffraction and nitrogen adsorption. It is confirmed that TiO2 shows a positive effect on the adsorption process of Na2CO3 and the reaction rate is observed to increase significantly, especially in the first 10 min. Moreover, TiO2 is stable within the temperature range of the process and no other Ti-compounds are detected. The carbonation products are NaHCO3 and Na5H3 （CO3 ）4. The surface area and the pore volume of the sorbent keep stable after 14 cycles. The Fourier transform infrared spectroscopy and the X-ray photoelectron spectroscopy are used to analyze the effect mechanism of TiO2 on CO2 adsorption process of Na2CO3/Al2O3.