yb^3＋：Er^3＋ co-doped oxy-fluoride ceramics glass has been prepared. The mechanism of up-conversion emissions about Er^3＋ was discussed, and the temperature properties of green up-conversion fluorescence between 30...yb^3＋：Er^3＋ co-doped oxy-fluoride ceramics glass has been prepared. The mechanism of up-conversion emissions about Er^3＋ was discussed, and the temperature properties of green up-conversion fluorescence between 303 and 823 K were investigated. The results show that the sensitivity of this sample reaches its maximum value, about 0.0047 K^-1, when the temperature is 383 K, indicating that this kind of sample can be used as high temperature and high sensitivity optical temperature sensor.展开更多
The glass sample based on the composition of 45PbF_2-45GeO_2-10WO_3 co-doped with Yb^(3+)/Er^(3+) was prepared by the fusion method in two steps: melted at 950 ℃ for 20～25 min then annealed at 380 ℃ for 4 h. Throug...The glass sample based on the composition of 45PbF_2-45GeO_2-10WO_3 co-doped with Yb^(3+)/Er^(3+) was prepared by the fusion method in two steps: melted at 950 ℃ for 20～25 min then annealed at 380 ℃ for 4 h. Through the V-prism it is found that the refractive index of host glass and the sample are 1.517 and 1.65 respectively. The transmittance was observed by using the ultraviolet-visible-infrared spectrometer in the wavelength range from 0.35 to 2.5μm. The transmittance of the host glass is beyond 73%. That of the sample is beyond 50% and there are characteristic absorption peaks of rare-earth ions. The emission spectrum was measured by using the Hitachi F-4500 fluorescent spectrometer pumped by 980 nm semiconductor laser. There are a strong emission peak at 530 nm and a weak peak at 650 nm.展开更多
Er^3 ＋/Yb^3 ＋ phosphate glasses were fabricated. According to McCumber theory, the stimulated emission cross-section of Er^3＋ ions at 1533 nm was calculated on the basis of absorption spectrum, and 0.84 × 10^-...Er^3 ＋/Yb^3 ＋ phosphate glasses were fabricated. According to McCumber theory, the stimulated emission cross-section of Er^3＋ ions at 1533 nm was calculated on the basis of absorption spectrum, and 0.84 × 10^-20 cm^2 is derived, the fluorescence lifetime of ^4I13/2 level is 8.5 ms. An Er^3＋/Yb^3＋ co-doped phosphate glass CW laser pumped by LD was demonstrated at room temperature. The maximum output power is 80 mW and slope efficiency is 16.5%.展开更多
The （60 - x）Bi2O3 - xGeO2-30B2O3-10ZnO （x = 5, 10, 20, 30 molar percent） glasses doped with Er^3＋ and Er^3＋/Yb^3＋ were fabricated using the melting method. The thermal stability of the glasses was studied with ...The （60 - x）Bi2O3 - xGeO2-30B2O3-10ZnO （x = 5, 10, 20, 30 molar percent） glasses doped with Er^3＋ and Er^3＋/Yb^3＋ were fabricated using the melting method. The thermal stability of the glasses was studied with their DTA curves. The results show that the difference between the glass transition temperature and the crystallization onset temperature increases with the increase of GeO2 content, indicating that the thermal stability of the glass has become better. The absorption spectra were recorded and the stimulated emission cross sections were calculated using the McCumber theory. The Ω2, O4, and Ω6 parameters,the transition probability, the radiative lifetime, and the fluorescence branch ratio of Er^3＋ for optical transition were calculated from their absorption spectra in terms of reduced matrix U^（t）（λ = 2, 4, 6） character for optical transitions. The infrared emission of Er^3＋ was measured upon excitation with 970 nm light and the full width at half-maximum （FWHM） was estimated from the emission spectra. The pumping efficiency and the intensity of the emission at the 1.54 μm band of Er^3＋ were enhanced considerably by co-doping Yb^3＋ .展开更多
The Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser d...The Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3＋/Er^3＋ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3＋/Er^3＋ is also studied, The luminescence intensity increases with the ratio of Yb^3＋/Er^3＋ increasing. The ratio of Yb^3＋/Er^3＋ plays a more important role than the concentration of Er^3＋ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3＋/Er^3＋ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.展开更多
The Er^3＋/yb^3＋ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy （TEM） images showed that CaF2 nano-...The Er^3＋/yb^3＋ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy （TEM） images showed that CaF2 nano-crystals of 20-30 nm in diameter precipitated uniformly in the glass matrix. luminescence of Er^3＋ at 540 nm and 658 nm was observed in Comparing with the host glass, high efficiency upconversion the glass ceramics under the excitation of 980 nm. Moreover, the size of the precipitated nano-crystals can be controlled by heat-treatment temperature and time. With the increase of the nano-crystal size, the intensity of the red emission increased more rapidly than that of the green emission. The energy transfer process of Er^3＋ and Yb^3＋ was convinced and the possible mechanism of Er^3＋ up-conversion was discussed.展开更多
The （60 - x） Bi2O3-xGeO2-30B2O3-10ZnO （x = 5, 10, 20, 30 molar percent） glasses doped with Er^3＋ and Er^3＋/Yb^3＋ were fabricated by melting method. The thermal stability of the glasses was studied by their DTA ...The （60 - x） Bi2O3-xGeO2-30B2O3-10ZnO （x = 5, 10, 20, 30 molar percent） glasses doped with Er^3＋ and Er^3＋/Yb^3＋ were fabricated by melting method. The thermal stability of the glasses was studied by their DTA curves. The results indicate that the difference between the glass transition temperature and the crystallization onset temperature increase as increase of GeO2 content, indicating that the thermal stability of the glass becomes better. The absorption spectra were recorded. The stimulated emission cross sections were calculated by McCumber theory. The Ω2, Ω4, and Ω6 parameters, transition probability, radiative lifetime, fluorescence branch ratio of Er^3＋ for optical transition were calculated from their absorption spectra in terms of reduced matrix U^（1）（λ = 2, 4, 6） character for optical transitions. The infrared emission was measured by excitation with 970 nm light and the FWHM was estimated from their emission spectra. The pumping efficiency and the intensity of emission at the band of 1.54 μm are enhanced greatly by addition of Y2O3.展开更多
Yb^3＋：Er^3＋：Tm^3＋co-doped borosilicate glasses are prepared. Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared, which are excited by a 978-nm laser diode, are meas...Yb^3＋：Er^3＋：Tm^3＋co-doped borosilicate glasses are prepared. Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared, which are excited by a 978-nm laser diode, are measured, and the mechanisms of energy transfer among Yb^3＋ Er^3＋ and Tm^3＋ ions are discussed. The results show that there is an unexpected wavelength at 900-nm emission from Yb^3＋ Stark splitting levels to pump Tm^3＋ ions and there exists an optimum pump power. The concentration of the Tm^3＋ dopant gives rise to a prominent effect on the intensity of visible and near-infrared emissions for the yb^3＋：Er^3＋：Tm^3＋ co-doped borosilicate glasses.展开更多
The energy transfer and upconversion of Er 3+ /Yb 3+ co-doped TeO2-TiO2-K2O glasses upon excitation with 976nm lasers diode were studied. The tellurite glasses were prepared by conventional melting methods. Their opti...The energy transfer and upconversion of Er 3+ /Yb 3+ co-doped TeO2-TiO2-K2O glasses upon excitation with 976nm lasers diode were studied. The tellurite glasses were prepared by conventional melting methods. Their optical properties and sensitization upconversion spectra were performed. The dependence of green upconversion luminescence intensity on the mole ratio of Yb 3+ to Er 3+ and Er 3+ concentration were discussed in detail. When the mole ratio of Yb 3+ to Er 3+ is 25/1 and Er 3+ concentration is 0.1% （mole fraction）, or when the mole ratio of Yb 3+ to Er 3+ is 10/1 and Er 3+ concentration is 0.15%, the optimal upconversion luminescence intensity is obtained. The obtained glasses can be one of the potential candidates for lasers-diode pumping microchip solid-state lasers.展开更多
An all-fiber based Er~ 3+ ∶Yb~ 3+ co-doped double clad fiber laser operating at 1550nm is demonstrated. By using 9m long Er~ 3+ ∶Yb~ 3+ co-doped fiber(EYDF) as the gain medium, and using a pair of fiber Bragg gratin...An all-fiber based Er~ 3+ ∶Yb~ 3+ co-doped double clad fiber laser operating at 1550nm is demonstrated. By using 9m long Er~ 3+ ∶Yb~ 3+ co-doped fiber(EYDF) as the gain medium, and using a pair of fiber Bragg gratings as wavelength filters, the line-width of the output laser is as narrow as 0.2nm and the output power is more than 6mW. The fluorescent effect of the laser before its emission is also studied. And it is found that the Er~ 3+ ∶Yb~ 3+ co-doped double-clad fiber laser also exhibits a high gain for Yb~ 3+ transition near 1080nm.展开更多
Based on propagation-rate equations, the influence of different input pulse durations on the properties of Er^3＋/Yb^3＋ co-doped double-clad fiber amplifier at dynamic equilibrium was analyzed. The change characteris...Based on propagation-rate equations, the influence of different input pulse durations on the properties of Er^3＋/Yb^3＋ co-doped double-clad fiber amplifier at dynamic equilibrium was analyzed. The change characteristic of output power sag with pulse duration and repetition rate was shown. Whether single or multichannel input pulses are amplified, the shorter the input pulse duration is, the smaller the power sags of output pulse will be. At low repetition rate, upper gain values（Gupper） of gain swing are almost the same for different input pulse durations, which tend to the small signal gain, but lower gain value（Glower） of short input pulse is larger than that of long input pulse. At highrepetition rate, lower gain value（Glower） approaches to upper gain value（Glower）.展开更多
Erbium-doped BaTiO3 films on LaNiO3/Si substrates were fabricated by sol-gel method. The crystalline structure, morphologies and upconversion （UC） luminescence properties of films were respectively investigated by X...Erbium-doped BaTiO3 films on LaNiO3/Si substrates were fabricated by sol-gel method. The crystalline structure, morphologies and upconversion （UC） luminescence properties of films were respectively investigated by X-ray diffraction （XRD）, atomic force microcopy （AFM） and photoluminescence （PL）. The results indicate that both of the microstructure and luminescence are found to be dependent on Er^3＋ substituting sites. The samples with A-site substitution have smaller lattice constants, larger grains and smoother surface than those with B-site substitution. The photoluminescence spectra show that both of the samples have two stronger green emission bands centered at 528 and 548 nm and a weak red emission band centered at 673 nm, which correspond to the relaxation of Er^3＋ from ^2H11/2, ^4S3/2, and ^4F9/2 levels to the ground level ^4I15/2, respectively. Compared with B-site doped films, A-site doped films have a stronger integrated intensity of green emissions and a weaker relative intensity of red emissions. The differences could be explained by the crystalline quality and cross relaxation （CR） process.展开更多
基金Project supported by the National Natural Science Foundation of China (Grant No. 10804015 )the Science Foundation of the Education Department of Liaoning Province of China (Grant No. 2009A417)
文摘yb^3＋：Er^3＋ co-doped oxy-fluoride ceramics glass has been prepared. The mechanism of up-conversion emissions about Er^3＋ was discussed, and the temperature properties of green up-conversion fluorescence between 303 and 823 K were investigated. The results show that the sensitivity of this sample reaches its maximum value, about 0.0047 K^-1, when the temperature is 383 K, indicating that this kind of sample can be used as high temperature and high sensitivity optical temperature sensor.
文摘The glass sample based on the composition of 45PbF_2-45GeO_2-10WO_3 co-doped with Yb^(3+)/Er^(3+) was prepared by the fusion method in two steps: melted at 950 ℃ for 20～25 min then annealed at 380 ℃ for 4 h. Through the V-prism it is found that the refractive index of host glass and the sample are 1.517 and 1.65 respectively. The transmittance was observed by using the ultraviolet-visible-infrared spectrometer in the wavelength range from 0.35 to 2.5μm. The transmittance of the host glass is beyond 73%. That of the sample is beyond 50% and there are characteristic absorption peaks of rare-earth ions. The emission spectrum was measured by using the Hitachi F-4500 fluorescent spectrometer pumped by 980 nm semiconductor laser. There are a strong emission peak at 530 nm and a weak peak at 650 nm.
文摘Er^3 ＋/Yb^3 ＋ phosphate glasses were fabricated. According to McCumber theory, the stimulated emission cross-section of Er^3＋ ions at 1533 nm was calculated on the basis of absorption spectrum, and 0.84 × 10^-20 cm^2 is derived, the fluorescence lifetime of ^4I13/2 level is 8.5 ms. An Er^3＋/Yb^3＋ co-doped phosphate glass CW laser pumped by LD was demonstrated at room temperature. The maximum output power is 80 mW and slope efficiency is 16.5%.
文摘The （60 - x）Bi2O3 - xGeO2-30B2O3-10ZnO （x = 5, 10, 20, 30 molar percent） glasses doped with Er^3＋ and Er^3＋/Yb^3＋ were fabricated using the melting method. The thermal stability of the glasses was studied with their DTA curves. The results show that the difference between the glass transition temperature and the crystallization onset temperature increases with the increase of GeO2 content, indicating that the thermal stability of the glass has become better. The absorption spectra were recorded and the stimulated emission cross sections were calculated using the McCumber theory. The Ω2, O4, and Ω6 parameters,the transition probability, the radiative lifetime, and the fluorescence branch ratio of Er^3＋ for optical transition were calculated from their absorption spectra in terms of reduced matrix U^（t）（λ = 2, 4, 6） character for optical transitions. The infrared emission of Er^3＋ was measured upon excitation with 970 nm light and the full width at half-maximum （FWHM） was estimated from the emission spectra. The pumping efficiency and the intensity of the emission at the 1.54 μm band of Er^3＋ were enhanced considerably by co-doping Yb^3＋ .
基金Project supported by the National Natural Science Foundation of China （Grant No 60307004） and the Science and Technology Program of Guangzhou, Guangdong province, China （Grant No 2004Z2-D0131）.
文摘The Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3＋/Er^3＋ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3＋/Er^3＋ is also studied, The luminescence intensity increases with the ratio of Yb^3＋/Er^3＋ increasing. The ratio of Yb^3＋/Er^3＋ plays a more important role than the concentration of Er^3＋ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3＋/Er^3＋ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.61265004,51272097,and 11204113)the Nature and Science Fund from Yunnan Province Ministry of Education,China(Grant No.2011C13211708)
文摘The Er^3＋/yb^3＋ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy （TEM） images showed that CaF2 nano-crystals of 20-30 nm in diameter precipitated uniformly in the glass matrix. luminescence of Er^3＋ at 540 nm and 658 nm was observed in Comparing with the host glass, high efficiency upconversion the glass ceramics under the excitation of 980 nm. Moreover, the size of the precipitated nano-crystals can be controlled by heat-treatment temperature and time. With the increase of the nano-crystal size, the intensity of the red emission increased more rapidly than that of the green emission. The energy transfer process of Er^3＋ and Yb^3＋ was convinced and the possible mechanism of Er^3＋ up-conversion was discussed.
文摘The （60 - x） Bi2O3-xGeO2-30B2O3-10ZnO （x = 5, 10, 20, 30 molar percent） glasses doped with Er^3＋ and Er^3＋/Yb^3＋ were fabricated by melting method. The thermal stability of the glasses was studied by their DTA curves. The results indicate that the difference between the glass transition temperature and the crystallization onset temperature increase as increase of GeO2 content, indicating that the thermal stability of the glass becomes better. The absorption spectra were recorded. The stimulated emission cross sections were calculated by McCumber theory. The Ω2, Ω4, and Ω6 parameters, transition probability, radiative lifetime, fluorescence branch ratio of Er^3＋ for optical transition were calculated from their absorption spectra in terms of reduced matrix U^（1）（λ = 2, 4, 6） character for optical transitions. The infrared emission was measured by excitation with 970 nm light and the FWHM was estimated from their emission spectra. The pumping efficiency and the intensity of emission at the band of 1.54 μm are enhanced greatly by addition of Y2O3.
基金Project supported by the National Natural Science Foundation of China (Grant No. 10804015)the Science Foundation of the Education Department of Liaoning Province of China (Grant No. 2009A417)
文摘Yb^3＋：Er^3＋：Tm^3＋co-doped borosilicate glasses are prepared. Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared, which are excited by a 978-nm laser diode, are measured, and the mechanisms of energy transfer among Yb^3＋ Er^3＋ and Tm^3＋ ions are discussed. The results show that there is an unexpected wavelength at 900-nm emission from Yb^3＋ Stark splitting levels to pump Tm^3＋ ions and there exists an optimum pump power. The concentration of the Tm^3＋ dopant gives rise to a prominent effect on the intensity of visible and near-infrared emissions for the yb^3＋：Er^3＋：Tm^3＋ co-doped borosilicate glasses.
基金Projects(2004Z2-D0131 and 2004A10602002) supported by the Science and Technology Programof Guangzhou , Guang-dong Province project(60307004 and 50472053) supported by the National Natural Science Foundation of China project(04200036) sup-ported by the Natural Foundation of Guangdong Province
文摘The energy transfer and upconversion of Er 3+ /Yb 3+ co-doped TeO2-TiO2-K2O glasses upon excitation with 976nm lasers diode were studied. The tellurite glasses were prepared by conventional melting methods. Their optical properties and sensitization upconversion spectra were performed. The dependence of green upconversion luminescence intensity on the mole ratio of Yb 3+ to Er 3+ and Er 3+ concentration were discussed in detail. When the mole ratio of Yb 3+ to Er 3+ is 25/1 and Er 3+ concentration is 0.1% （mole fraction）, or when the mole ratio of Yb 3+ to Er 3+ is 10/1 and Er 3+ concentration is 0.15%, the optimal upconversion luminescence intensity is obtained. The obtained glasses can be one of the potential candidates for lasers-diode pumping microchip solid-state lasers.
文摘An all-fiber based Er~ 3+ ∶Yb~ 3+ co-doped double clad fiber laser operating at 1550nm is demonstrated. By using 9m long Er~ 3+ ∶Yb~ 3+ co-doped fiber(EYDF) as the gain medium, and using a pair of fiber Bragg gratings as wavelength filters, the line-width of the output laser is as narrow as 0.2nm and the output power is more than 6mW. The fluorescent effect of the laser before its emission is also studied. And it is found that the Er~ 3+ ∶Yb~ 3+ co-doped double-clad fiber laser also exhibits a high gain for Yb~ 3+ transition near 1080nm.
文摘Based on propagation-rate equations, the influence of different input pulse durations on the properties of Er^3＋/Yb^3＋ co-doped double-clad fiber amplifier at dynamic equilibrium was analyzed. The change characteristic of output power sag with pulse duration and repetition rate was shown. Whether single or multichannel input pulses are amplified, the shorter the input pulse duration is, the smaller the power sags of output pulse will be. At low repetition rate, upper gain values（Gupper） of gain swing are almost the same for different input pulse durations, which tend to the small signal gain, but lower gain value（Glower） of short input pulse is larger than that of long input pulse. At highrepetition rate, lower gain value（Glower） approaches to upper gain value（Glower）.
基金Project (2009AA035002) supported by the High-tech Research and Development Program of China
文摘Erbium-doped BaTiO3 films on LaNiO3/Si substrates were fabricated by sol-gel method. The crystalline structure, morphologies and upconversion （UC） luminescence properties of films were respectively investigated by X-ray diffraction （XRD）, atomic force microcopy （AFM） and photoluminescence （PL）. The results indicate that both of the microstructure and luminescence are found to be dependent on Er^3＋ substituting sites. The samples with A-site substitution have smaller lattice constants, larger grains and smoother surface than those with B-site substitution. The photoluminescence spectra show that both of the samples have two stronger green emission bands centered at 528 and 548 nm and a weak red emission band centered at 673 nm, which correspond to the relaxation of Er^3＋ from ^2H11/2, ^4S3/2, and ^4F9/2 levels to the ground level ^4I15/2, respectively. Compared with B-site doped films, A-site doped films have a stronger integrated intensity of green emissions and a weaker relative intensity of red emissions. The differences could be explained by the crystalline quality and cross relaxation （CR） process.