Blue-green luminescent BaAl2O4：Eu2＋,Dy3＋ phosphor powders were synthesized via combustion synthesis method assisted by microwave irradiation in air. The phosphors were characterized by X-ray diffraction （XRD）, sc...Blue-green luminescent BaAl2O4：Eu2＋,Dy3＋ phosphor powders were synthesized via combustion synthesis method assisted by microwave irradiation in air. The phosphors were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and fluorescence spectrophotometer. The XRD results revealed that when the concentration of urea was over 3 times higher than theoretical quantities, a BaAl2O4 single hexagonal phase was obtained. The SEM results revealed that the surface of the BaAl2O4：Eu2＋,Dy3＋ powder samples showed lots of voids and pores. The BaAl2O4：Eu2＋,Dy3＋ phosphors exhibited a broad emission band of main peak at 496 nm and a shoulder peak at 426 nm under excitation of 337 nm. The BaAl2O4：Eu2＋,Dy3＋ phosphors at the Eu2＋ concentration of 1 mol.% showed the strongest luminescent intensity. Long afterglow phosphorescence was observed in the dark with naked eyes after the removal of the excitation source.展开更多
Novel red-emitting phosphors Sr2MgSi2O7：Eu3＋ were prepared by gel-combustion method assisted by microwave. The phase struc-ture and luminescent properties of as-synthesized phosphors were investigated by XRD and flu...Novel red-emitting phosphors Sr2MgSi2O7：Eu3＋ were prepared by gel-combustion method assisted by microwave. The phase struc-ture and luminescent properties of as-synthesized phosphors were investigated by XRD and fluorescence spectrophotometer, respectively. The results showed that the as-synthesized sample was Sr2MgSi2O7 with tetragonal crystal structure. The excitation spectrum of Sr2MgSi2O7：Eu3＋ was composed of two major parts： one was the broad band between 200 and 350 nm, which belonged to the charge transfer of Eu3＋-O2-; the other consisted of a series of sharp lines between 350 and 450 nm, ascribed to the f-f transition of Eu3＋. The emission spec-trum consisted of two emission peaks at 593 and 616 nm, which was attributed to 5D0→7F1 and 5D0→7F2 of Eu3＋, respectively. The concen-tration of Eu3＋ （x） had great effect on the emission intensity of Sr2-xMgSi2O7：Eu3＋x. When x varied in the range of 0.04-0.18, the intensity of emission peaks at 593 and 616 nm increased gradually with the concentration of Eu3＋ increasing. It was interesting that no concentration quenching occurred. Moreover, the luminescent intensity could be greatly enhanced with incorporation of charge compensator Li＋ ions.展开更多
基金supported by the National Natural Science Foundation of China (60477034)
文摘Blue-green luminescent BaAl2O4：Eu2＋,Dy3＋ phosphor powders were synthesized via combustion synthesis method assisted by microwave irradiation in air. The phosphors were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and fluorescence spectrophotometer. The XRD results revealed that when the concentration of urea was over 3 times higher than theoretical quantities, a BaAl2O4 single hexagonal phase was obtained. The SEM results revealed that the surface of the BaAl2O4：Eu2＋,Dy3＋ powder samples showed lots of voids and pores. The BaAl2O4：Eu2＋,Dy3＋ phosphors exhibited a broad emission band of main peak at 496 nm and a shoulder peak at 426 nm under excitation of 337 nm. The BaAl2O4：Eu2＋,Dy3＋ phosphors at the Eu2＋ concentration of 1 mol.% showed the strongest luminescent intensity. Long afterglow phosphorescence was observed in the dark with naked eyes after the removal of the excitation source.
基金Project supported by the National Natural Science Foundation of China (20675023)
文摘Novel red-emitting phosphors Sr2MgSi2O7：Eu3＋ were prepared by gel-combustion method assisted by microwave. The phase struc-ture and luminescent properties of as-synthesized phosphors were investigated by XRD and fluorescence spectrophotometer, respectively. The results showed that the as-synthesized sample was Sr2MgSi2O7 with tetragonal crystal structure. The excitation spectrum of Sr2MgSi2O7：Eu3＋ was composed of two major parts： one was the broad band between 200 and 350 nm, which belonged to the charge transfer of Eu3＋-O2-; the other consisted of a series of sharp lines between 350 and 450 nm, ascribed to the f-f transition of Eu3＋. The emission spec-trum consisted of two emission peaks at 593 and 616 nm, which was attributed to 5D0→7F1 and 5D0→7F2 of Eu3＋, respectively. The concen-tration of Eu3＋ （x） had great effect on the emission intensity of Sr2-xMgSi2O7：Eu3＋x. When x varied in the range of 0.04-0.18, the intensity of emission peaks at 593 and 616 nm increased gradually with the concentration of Eu3＋ increasing. It was interesting that no concentration quenching occurred. Moreover, the luminescent intensity could be greatly enhanced with incorporation of charge compensator Li＋ ions.