Using high-speed oil-filled spinning method,high quality micro copper tube with straight grooves（MCTSG） with an outer diameter of 6 mm was obtained.Then,MCTSG with an outer diameter of 3-6 mm was fabricated successf...Using high-speed oil-filled spinning method,high quality micro copper tube with straight grooves（MCTSG） with an outer diameter of 6 mm was obtained.Then,MCTSG with an outer diameter of 3-6 mm was fabricated successfully by multi-pass drawing processing method.The influence of drawing parameters on the forming of micro straight grooves was investigated based on the forming mechanism.The results show that the values of groove depth and width decrease,while the wall thickness increases as the drawing diameter decreases.At the same time,the groove depth and width increase,while the wall thickness decreases as the die angle increases.The drawing force increases as the reduction increases.Excessive copper tube reduction may results in groove folding and segmental teeth.The drawing force decreases firstly and then increases with the increases in die angle.When the die angle α is 16°,the drawing force is the smallest,indicating 16° is the optimal angle.展开更多
A procedure of low temperature solid-phase sintering（LTSS） was carried out to fabricate sintered metal fibrous media（SMFM） with high specific surface area.Stainless steel fibers which were produced by cutting proc...A procedure of low temperature solid-phase sintering（LTSS） was carried out to fabricate sintered metal fibrous media（SMFM） with high specific surface area.Stainless steel fibers which were produced by cutting process were first plated with a coarse copper coating layer by electroless plating process.A low-temperature sintering process was then completed at about 800 °C for 1 h under the protection of hydrogen atmosphere.The results show that a novel SMFM with complex surface morphology and high specific surface area（0.2 m2/g） can be obtained in this way.The effect of sintering temperature on the surface morphology and specific surface area of SMFM was studied by means of scanning electron microscopy and Brunauer-Emmett-Teller.The damage of micro-structure during the sintering process mainly contributed to the loss of specific surface area of SMFM and the optimal sintering temperature was 800 °C.展开更多
The intensified boiling and condensation wick structures of heat column were designed and manufactured by ploughing-extrusion （P-E） machining method.The forming process and mechanism were analyzed.The results show t...The intensified boiling and condensation wick structures of heat column were designed and manufactured by ploughing-extrusion （P-E） machining method.The forming process and mechanism were analyzed.The results show that the P-E depth plays a decisive role in forming of wick structure.The larger the P-E depth is,the better the surface characteristics are.Only when the groove spacing is in a certain range,superior surface structure can be formed in the wick.The better enhancement boiling structure forms at P-E depth of 0.3 mm,ringed groove spacing of 0.4 mm,and interior angle of radial groove of 3°;the better enhancement condensation structure forms at P-E depth of 0.3 mm,ringed groove spacing of 0.4 mm,and axial grooves spacing of π/3 mm.展开更多
A rotary swaging machine was applied to fabricating pipe reduction for miniature inner grooved copper tube （MIGCT） heat pipes. Compared with conventional swaging method, the axial feed of the designed rotary swaging...A rotary swaging machine was applied to fabricating pipe reduction for miniature inner grooved copper tube （MIGCT） heat pipes. Compared with conventional swaging method, the axial feed of the designed rotary swaging machine was reached by a constant pushing force. The deformation of grooves in pipe reduced section during rotary swaging was analyzed. The shrinkage and extensibility of pipe reduction were measured and calculated. Furthermore, four aspects, including outer diameter, surface roughness, extensibility and processing time of pipe reduction, which were influenced by the pushing force, were considered. The results show that the tube wall thickness increases gradually along the z-axis at sinking section. However, the outer diameters, surface roughness and micro-cracks at reduced section tend to decrease along the z-axis. Besides, the effect of variation in the pushing force on the extensibility is limited while an increase in the pushing force results in a decrease of surface roughness. Therefore, a large pushing force within the limit is beneficial to pipe reduction manufacturing during rotary swaging process.展开更多
To investigate the workpiece curvature influence on groove deformation,numerical studies with curvature varying from negative to positive were conducted on copper material.Groove deformations were analyzed,including g...To investigate the workpiece curvature influence on groove deformation,numerical studies with curvature varying from negative to positive were conducted on copper material.Groove deformations were analyzed,including groove geometry,effective stress distribution and plough force.The curled groove shape whose workpiece curvature was 0.133 mm-1 was validated by experiments.Moreover,a series of geometry models with various curvatures were introduced to analyze the change of groove deformation.The results show that positive curvatures influence groove deformation more intensively than negative or zero curvature.It is mainly due to the action of the tool forming face during plough process.展开更多
基金Project(U0834002)supported by the Joint Funds of NSFC-Guangdong of ChinaProject(2009ZM0121)supported by the Fundamental Research Funds for the Central Universities,ChinaProjects(LYM09024)supported by Training Program for Excellent Young Teachers with Innovation of Guangdong University,China
文摘Using high-speed oil-filled spinning method,high quality micro copper tube with straight grooves（MCTSG） with an outer diameter of 6 mm was obtained.Then,MCTSG with an outer diameter of 3-6 mm was fabricated successfully by multi-pass drawing processing method.The influence of drawing parameters on the forming of micro straight grooves was investigated based on the forming mechanism.The results show that the values of groove depth and width decrease,while the wall thickness increases as the drawing diameter decreases.At the same time,the groove depth and width increase,while the wall thickness decreases as the die angle increases.The drawing force increases as the reduction increases.Excessive copper tube reduction may results in groove folding and segmental teeth.The drawing force decreases firstly and then increases with the increases in die angle.When the die angle α is 16°,the drawing force is the smallest,indicating 16° is the optimal angle.
基金Project (50930005) supported by the National Natural Science Foundation of ChinaProject (U0834002) supported by the Key Programof NSFC-Guangdong Joint Funds of China+1 种基金Project (LYM09024) supported by Training Program for Excellent Young Teachers withInnovation of Guangdong University, ChinaProject (2009ZM0121) supported by the Fundamental Research Funds for the CentralUniversities of South China University of Technology,China
文摘A procedure of low temperature solid-phase sintering（LTSS） was carried out to fabricate sintered metal fibrous media（SMFM） with high specific surface area.Stainless steel fibers which were produced by cutting process were first plated with a coarse copper coating layer by electroless plating process.A low-temperature sintering process was then completed at about 800 °C for 1 h under the protection of hydrogen atmosphere.The results show that a novel SMFM with complex surface morphology and high specific surface area（0.2 m2/g） can be obtained in this way.The effect of sintering temperature on the surface morphology and specific surface area of SMFM was studied by means of scanning electron microscopy and Brunauer-Emmett-Teller.The damage of micro-structure during the sintering process mainly contributed to the loss of specific surface area of SMFM and the optimal sintering temperature was 800 °C.
基金Project(U0834002) supported by the Joint Funds of NSFC-Guangdong of ChinaProject(2009ZM0121) supported by the Fundamental Research Funds for the Central Universities,China
文摘The intensified boiling and condensation wick structures of heat column were designed and manufactured by ploughing-extrusion （P-E） machining method.The forming process and mechanism were analyzed.The results show that the P-E depth plays a decisive role in forming of wick structure.The larger the P-E depth is,the better the surface characteristics are.Only when the groove spacing is in a certain range,superior surface structure can be formed in the wick.The better enhancement boiling structure forms at P-E depth of 0.3 mm,ringed groove spacing of 0.4 mm,and interior angle of radial groove of 3°;the better enhancement condensation structure forms at P-E depth of 0.3 mm,ringed groove spacing of 0.4 mm,and axial grooves spacing of π/3 mm.
基金Project (U0834002) supported by the Key Program of NSFC Guangdong Joint Funds of ChinaProjects (51005079, 20976055) supported by the National Natural Science Foundation of China+1 种基金Project (10451064101005146) supported by the Natural Science Foundation of Guangdong Province, ChinaProject (20100172120001) supported by Specialized Research Fund for the Doctoral Program of Higher Education, China
文摘A rotary swaging machine was applied to fabricating pipe reduction for miniature inner grooved copper tube （MIGCT） heat pipes. Compared with conventional swaging method, the axial feed of the designed rotary swaging machine was reached by a constant pushing force. The deformation of grooves in pipe reduced section during rotary swaging was analyzed. The shrinkage and extensibility of pipe reduction were measured and calculated. Furthermore, four aspects, including outer diameter, surface roughness, extensibility and processing time of pipe reduction, which were influenced by the pushing force, were considered. The results show that the tube wall thickness increases gradually along the z-axis at sinking section. However, the outer diameters, surface roughness and micro-cracks at reduced section tend to decrease along the z-axis. Besides, the effect of variation in the pushing force on the extensibility is limited while an increase in the pushing force results in a decrease of surface roughness. Therefore, a large pushing force within the limit is beneficial to pipe reduction manufacturing during rotary swaging process.
基金Project (U0834002) supported by the Key Program of NSFC-Guangdong Joint Funds of ChinaProject (51005079) supported by the National Natural Science Foundation of China+1 种基金Project (20100172120001) supported by Specialized Research Fund for the Doctoral Program of Higher Education, ChinaProject (10451064101005146) supported by the Natural Science Foundation of Guangdong Province,China
文摘To investigate the workpiece curvature influence on groove deformation,numerical studies with curvature varying from negative to positive were conducted on copper material.Groove deformations were analyzed,including groove geometry,effective stress distribution and plough force.The curled groove shape whose workpiece curvature was 0.133 mm-1 was validated by experiments.Moreover,a series of geometry models with various curvatures were introduced to analyze the change of groove deformation.The results show that positive curvatures influence groove deformation more intensively than negative or zero curvature.It is mainly due to the action of the tool forming face during plough process.
基金National Nature Science Foundation of China(51275180)Major State Basic Research Development Program of China("973" Program)(2011CB710703)Fundamental Research Funds for the Central Universities,SCUT(2013ZZ017)