WC powders were uniformly coated by Ni nanoparticles through a combined chemical co-precipitation and subsequent high temperature hydrogen reduction strategy(abbreviated as CM-WCN),and then were consolidated by vacuum...WC powders were uniformly coated by Ni nanoparticles through a combined chemical co-precipitation and subsequent high temperature hydrogen reduction strategy(abbreviated as CM-WCN),and then were consolidated by vacuum sintering at 1450°C for 1 h to obtain WC−Ni cemented carbides.The microstructure and properties of the as-consolidated CM-WCN were investigated.The average grain size of WC in the consolidated CM-WCN was calculated to be in the range of 3.0−3.8μm and only few pores were observed.A relative density of 99.6%,hardness of HRA 86.5 and bending strength of 1860 MPa were obtained for the CM-WCN−10wt.%Ni,and the highest impact toughness of 6.17 J/cm^(2 )was obtained for the CM-WCN−12wt.%Ni,surpassing those of the hand mixed WC−Ni(HM-WCN)cemented carbides examined in this study and the other similar materials in the literature.CM-WCN cemented carbides possess excellent mechanical properties,due to their highly uniform structure and low porosity that could be ascribed to the intergranular-dominated fracture mode accompanied by a large number of plastic deformation tears of the bonding phase.In addition,the corrosion resistance of CM-WCN was superior to that of HM-WCN at the Ni content of 6−12 wt.%.展开更多
To investigate the effect of separate Al_(2)Ca and Mg_(2)Ca phases on the corrosion properties of Mg−Al−Ca−Mn alloys,OM,SEM,immersion and electrochemical tests were conducted on the as-cast and ECAP Al_(2)Ca-containin...To investigate the effect of separate Al_(2)Ca and Mg_(2)Ca phases on the corrosion properties of Mg−Al−Ca−Mn alloys,OM,SEM,immersion and electrochemical tests were conducted on the as-cast and ECAP Al_(2)Ca-containing(2Ca)and Mg_(2)Ca-containing(4Ca)alloys.At the beginning of corrosion,the two as-cast alloys are corroded slowly compared with ECAP alloys.With prolonging the corrosion time,the corrosion of ECAP alloys becomes slighter than that of as-cast alloys,which is mainly ascribed to the dispersion and refinement of the second phase in ECAP alloys.Moreover,the corrosion degree of 2Ca alloys is always slighter than that of 4Ca alloys,suggesting that Al_(2)Ca phase is more beneficial to the enhancement of corrosion resistance of Mg−Al−Ca−Mn based alloys than Mg_(2)Ca phase.Finally,based on the examinations of corrosion surface and electrochemical testing results,different corrosion mechanisms caused by the distributions and morphology of Al_(2)Ca and Mg_(2)Ca phases are discussed.展开更多
In the current study,an effort has been taken to manufacture and compare the characteristics of functionally graded tubes. Two samples have been produced with a commercially pure aluminium matrix reinforced by 10%(in ...In the current study,an effort has been taken to manufacture and compare the characteristics of functionally graded tubes. Two samples have been produced with a commercially pure aluminium matrix reinforced by 10%(in weight) SiC and Al_(2)O_(3)with a 16 μm average size via horizontal centrifugal casting. In addition to microstructure analysis,the mechanical and wear characteristics have been investigated across the thickness of the produced tubes.The results showed that the addition of SiC and Al_(2)O_(3)particles relative to the unreinforced matrix(pure Al)significantly enhance the mechanical properties and wear resistance of the produced tubes. Thus,these tubes are the best choice for automobile applications.展开更多
基金the financial supports from the National Natural Science Foundation of China (Nos. 51778213, 52078189)the Fundamental Research Funds for the Central Universities, China (No. B200202073)。
文摘WC powders were uniformly coated by Ni nanoparticles through a combined chemical co-precipitation and subsequent high temperature hydrogen reduction strategy(abbreviated as CM-WCN),and then were consolidated by vacuum sintering at 1450°C for 1 h to obtain WC−Ni cemented carbides.The microstructure and properties of the as-consolidated CM-WCN were investigated.The average grain size of WC in the consolidated CM-WCN was calculated to be in the range of 3.0−3.8μm and only few pores were observed.A relative density of 99.6%,hardness of HRA 86.5 and bending strength of 1860 MPa were obtained for the CM-WCN−10wt.%Ni,and the highest impact toughness of 6.17 J/cm^(2 )was obtained for the CM-WCN−12wt.%Ni,surpassing those of the hand mixed WC−Ni(HM-WCN)cemented carbides examined in this study and the other similar materials in the literature.CM-WCN cemented carbides possess excellent mechanical properties,due to their highly uniform structure and low porosity that could be ascribed to the intergranular-dominated fracture mode accompanied by a large number of plastic deformation tears of the bonding phase.In addition,the corrosion resistance of CM-WCN was superior to that of HM-WCN at the Ni content of 6−12 wt.%.
基金financial supports from the National Natural Science Foundation of China (Nos.51901068,51979099)the Key Research and Development Project of Jiangsu Province,China (No.BE2021027)+1 种基金the Opening Project of Jiangsu Key Laboratory of Advanced Structural Materials and Application Technology,China (No.ASMA202102)the Research Fund from Key Laboratory for Light-weight Materials of Jiangsu Province,China。
文摘To investigate the effect of separate Al_(2)Ca and Mg_(2)Ca phases on the corrosion properties of Mg−Al−Ca−Mn alloys,OM,SEM,immersion and electrochemical tests were conducted on the as-cast and ECAP Al_(2)Ca-containing(2Ca)and Mg_(2)Ca-containing(4Ca)alloys.At the beginning of corrosion,the two as-cast alloys are corroded slowly compared with ECAP alloys.With prolonging the corrosion time,the corrosion of ECAP alloys becomes slighter than that of as-cast alloys,which is mainly ascribed to the dispersion and refinement of the second phase in ECAP alloys.Moreover,the corrosion degree of 2Ca alloys is always slighter than that of 4Ca alloys,suggesting that Al_(2)Ca phase is more beneficial to the enhancement of corrosion resistance of Mg−Al−Ca−Mn based alloys than Mg_(2)Ca phase.Finally,based on the examinations of corrosion surface and electrochemical testing results,different corrosion mechanisms caused by the distributions and morphology of Al_(2)Ca and Mg_(2)Ca phases are discussed.
文摘In the current study,an effort has been taken to manufacture and compare the characteristics of functionally graded tubes. Two samples have been produced with a commercially pure aluminium matrix reinforced by 10%(in weight) SiC and Al_(2)O_(3)with a 16 μm average size via horizontal centrifugal casting. In addition to microstructure analysis,the mechanical and wear characteristics have been investigated across the thickness of the produced tubes.The results showed that the addition of SiC and Al_(2)O_(3)particles relative to the unreinforced matrix(pure Al)significantly enhance the mechanical properties and wear resistance of the produced tubes. Thus,these tubes are the best choice for automobile applications.